Microstructure, martensitic transformation and superelasticity of T1(49) (6)N1(45 1)Cu(5)Cr(0 3) shape memory alloy | |
Wang, Q. Y. ; Zheng, Y. F. ; Liu, Y. | |
刊名 | 材料快报
![]() |
2011 | |
关键词 | Shape memory materials Martensitic transformation Mechanical properties Metals and alloys MECHANICAL-PROPERTIES ORTHODONTIC WIRES NITI BEHAVIOR TEMPERATURES DEPENDENCE ARCHWIRES |
DOI | 10.1016/j.matlet.2010.09.036 |
英文摘要 | The aim of this study is to investigate the microstructure martensitic transformation behavior shape memory effect and superelastic property of N1(45) 1Cu5Cr0 3 alloy with Cu and Cr substituting for Ni After annealing the alloy showed single step A-M/M-A transformations within the whole annealing temperature range of 623 K to 1273 K even in the presence and 112(Ni Cu) precipitates With the increase of the annealing temperature the transformation temperatures exhibited three stages increasing from 623 K to 873 K decreasing from 873 K to 1023 K and unchanging from 1023 K to 1273 K Meanwhile the critical stress for stress Induced martensitic (SIM) transformation decreased to a minimum value and increased after that exhibiting a V shape curve The alloy annealed at 623 773 and 923 K exhibited shape recovery ratio more than 90% when the deformation strain was below 20% (C) 2010 Elsevier B V All rights reserved; Materials Science, Multidisciplinary; Physics, Applied; SCI(E); EI; 7; ARTICLE; 1; 74-77; 65 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/243209] ![]() |
专题 | 工学院 |
推荐引用方式 GB/T 7714 | Wang, Q. Y.,Zheng, Y. F.,Liu, Y.. Microstructure, martensitic transformation and superelasticity of T1(49) (6)N1(45 1)Cu(5)Cr(0 3) shape memory alloy[J]. 材料快报,2011. |
APA | Wang, Q. Y.,Zheng, Y. F.,&Liu, Y..(2011).Microstructure, martensitic transformation and superelasticity of T1(49) (6)N1(45 1)Cu(5)Cr(0 3) shape memory alloy.材料快报. |
MLA | Wang, Q. Y.,et al."Microstructure, martensitic transformation and superelasticity of T1(49) (6)N1(45 1)Cu(5)Cr(0 3) shape memory alloy".材料快报 (2011). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论