In vitro and in vivo studies on Ti-based bulk metallic glass as potential dental implant material | |
Wang, Y. B. ; Li, H. F. ; Cheng, Y. ; Zheng, Y. F. ; Ruan, L. Q. | |
刊名 | materials science engineering c materials for biological applications
![]() |
2013 | |
关键词 | TiZrHfCuNiSiSn alloy Bulk metallic glass In vitro In vivo BIOMEDICAL APPLICATIONS AMORPHOUS-ALLOYS FORMING ABILITY CYTOTOXICITY BIOCOMPATIBILITY IONS BEHAVIOR CELLS |
DOI | 10.1016/j.msec.2013.04.038 |
英文摘要 | In this study, a high glass forming system, Ti41.5Zr2.5Hf5Cu37.5Ni7.5Si1Sn5 (TZHCNSS) bulk metallic glass (BMG), is studied in terms of microstructure, surface analysis, mechanical properties, corrosion resistance, in vitro cytotoxicity and in vivo biocompatibility. It is found that the as-prepared TZHCNSS samples are fully amorphous by XRD and TEM observations, as well as DSC curve. Comparing with pure Ti, TZHCNSS BMG shows superior mechanical properties with higher hardness and better wear resistance. Due to the oxide film formed on its surface, TZHCNSS BMG shows great corrosion resistance close to pure Ti in electrochemical measurements. The pitting corrosion potential in artificial saliva solution is much higher than that in SBF solution. The indirect and direct cytotoxicity results show that TZHCNSS extracts had obvious low cell viability on both L929 and NIH3T3 cells. However, the in vivo testing results proved that TZHCNSS BMG could integrate with bone tissue, showing excellent osseointegration. (c) 2013 Elsevier B.V. All rights reserved.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000320973000050&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Materials Science, Biomaterials; SCI(E); EI; PubMed; 12; ARTICLE; 6; 3489-3497; 33 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/153890] ![]() |
专题 | 工学院 |
推荐引用方式 GB/T 7714 | Wang, Y. B.,Li, H. F.,Cheng, Y.,et al. In vitro and in vivo studies on Ti-based bulk metallic glass as potential dental implant material[J]. materials science engineering c materials for biological applications,2013. |
APA | Wang, Y. B.,Li, H. F.,Cheng, Y.,Zheng, Y. F.,&Ruan, L. Q..(2013).In vitro and in vivo studies on Ti-based bulk metallic glass as potential dental implant material.materials science engineering c materials for biological applications. |
MLA | Wang, Y. B.,et al."In vitro and in vivo studies on Ti-based bulk metallic glass as potential dental implant material".materials science engineering c materials for biological applications (2013). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论