	Fabrication of Li-doped ZnO nanoparticles in aqueous solution and their ferroelectricity-like behavior
	Yin, Jianbo ; Zhang, Gengmin
	2012
关键词	ferroelectricity ZnO Li doping PULSED-LASER DEPOSITION RAMAN-SPECTROSCOPY THIN-FILMS TRANSITION
英文摘要	Li-doped ZnO nanoparticles were fabricated in aqueous solution of zinc nitrate and hexamethylenetetramine (HMTA) to which lithium chloride was added. SEM, XRD and TEM results revealed that the as-synthesized nanoparticles were crystalline wurzite ZnO with hexagonal flake morphology. ICP analysis confirmed the existence of Li element in these ZnO nanoparticles. For the measurement on their dielectric properties, the nanoparticles were further annealed in air under 900 degrees C for 1 hour and then pressed into tablets under a pressure of 5x10(3) kg/cm(2). When voltage cycles with varying magnitude were applied to these tablets of the Li-doped ZnO nanoparticles, the dependence of the polarization versus the applied field turned out to be hysteresis loops. The remanent polarizations and coercive fields were measured to be 10(-5) to 10(-4) Cm-2 and 10(4) to 10(5) Vm(-1) order of magnitude, respectively. Since a variety of phenomena other than ferroelectricity would also lead to hysteresis loops, similar measurements for comparison were further performed with a view to probing the origin of the observed loops. The dielectric behaviors of ZnO nanoparticles fabricated in the Li-free solutions and the commercial ZnO particles were also measured and the polarization-field plots both appeared to be straight lines instead of loops.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000313016400006&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Engineering, Electrical & Electronic; Materials Science, Multidisciplinary; Physics, Applied; EI; CPCI-S(ISTP); 0
语种	英语
DOI标识	10.1109/ISAF.2012.6297720
内容类型	其他
源URL	[http://ir.pku.edu.cn/handle/20.500.11897/406004]
专题	信息科学技术学院
推荐引用方式 GB/T 7714	Yin, Jianbo,Zhang, Gengmin. Fabrication of Li-doped ZnO nanoparticles in aqueous solution and their ferroelectricity-like behavior. 2012-01-01.

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。