Investigative studies for inert transformation of toxic chrysotile tailing | |
Zhu, P. ; Wang, L. Y. ; Hong, D. ; Zhou, M. ; Zhou, J. | |
刊名 | journal of material cycles and waste management
![]() |
2013 | |
关键词 | Chrysotile tailing waste Kaolin tailing waste Cordierite ceramics Recycling CORDIERITE POWDER ASBESTOS CERAMICS KAOLIN MECHANISM ALUMINA WASTE TALC ASH |
DOI | 10.1007/s10163-012-0093-6 |
英文摘要 | In an attempt to find ways to reduce consumption of natural raw material and recycle chrysotile tailing waste (CTW), cordierite ceramics were produced using CTW, kaolin tailing waste (KTW) and waste alumina. Before synthesizing the cordierite ceramics, the inert transformation of CTW was investigated via a thermal treatment. Experimental results indicated that CTW was converted into nonhazardous forsterite and enstatite at temperatures above 1000 A degrees C. The characterizations of the synthesized cordierite ceramics were examined using thermal analyses, X-ray diffraction (XRD), morphological structure analyses, compressive strength measurement, coefficient of thermal expansion (CTE) and toxicity characteristic leaching procedure (TCLP). Thermal analyses indicated that significant weight loss below 900 A degrees C was the release of structural water and gases. XRD indicated that the cordierite became the main crystalline phase at 1350 A degrees C. Compressive strength test indicated that compressive strength of the cordierite ceramics was 260 MPa, and CTE of cordierite ceramics was 2.4 x 10(-6) A degrees C-1. This technology for the of utilization of CTW and KTW could be used to produce industrial cordierite ceramics, in accordance with the concepts of sustainable development.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000314043200011&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Environmental Sciences; SCI(E); 4; ARTICLE; 1; 90-97; 15 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/291274] ![]() |
专题 | 信息科学技术学院 |
推荐引用方式 GB/T 7714 | Zhu, P.,Wang, L. Y.,Hong, D.,et al. Investigative studies for inert transformation of toxic chrysotile tailing[J]. journal of material cycles and waste management,2013. |
APA | Zhu, P.,Wang, L. Y.,Hong, D.,Zhou, M.,&Zhou, J..(2013).Investigative studies for inert transformation of toxic chrysotile tailing.journal of material cycles and waste management. |
MLA | Zhu, P.,et al."Investigative studies for inert transformation of toxic chrysotile tailing".journal of material cycles and waste management (2013). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论