Preparation and characteristics of NiO-coated nano-fibriform silica | |
Li, Xuejun ; Xiao, Zhiyong ; Lu, Anhuai ; Wang, Lijuan ; Ouyang, Xihui ; Ma, Junhong ; Li, Yuanyuan | |
刊名 | colloids and surfaces a physicochemical and engineering aspects
![]() |
2008 | |
关键词 | nano-fibriform silica NiO catalyst catalyst carrier NATURAL CHRYSOTILE THERMAL-STABILITY NI/SIO2 CATALYST GEL OXIDE |
DOI | 10.1016/j.colsurfa.2008.04.011 |
英文摘要 | NiO-coated nano-fibriform silica (NFS) was prepared by an excessive soakage method and was characterized using transmission electron Microscopy, X-ray diffraction, and physical N-2 adsorption techniques Linder different conditions. The results demonstrate that the coated NiO is of a cubic crystal form. The best preparation conditions are incubation in a water bath at 95 C for 2 It and drying at 45 C for 17 h, which lead to a higher NFS utilization ratio and thus lower cost, and a well-distributed NiO coating on the carrier NFS. Nitrogen adsorption isotherms for NiO-coated NFS are similar to a type IV curve, with a specific surface area of 292.7 m(2)/g, adsorptive capacity of 379.2 cm(3)/g, and Pore volume of 0.59 cm(3)/g. The average pore diameter of NiO-coated NFS is 8.01 nm, but most pore diameters are in the range 2.1-3.9 nm. Comparison of NiO-coated NFS and NiO(Ni)-coated sol-gel silica as catalysts reveals that NiO-coated NFS may be an effective catalyst and that NFS may be a good catalyst carrier. (C) 2008 Elsevier- B.V. All rights reserved.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000257908600029&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Chemistry, Physical; SCI(E); EI; 5; ARTICLE; 1-3; 171-175; 324 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/248748] ![]() |
专题 | 地球与空间科学学院 |
推荐引用方式 GB/T 7714 | Li, Xuejun,Xiao, Zhiyong,Lu, Anhuai,et al. Preparation and characteristics of NiO-coated nano-fibriform silica[J]. colloids and surfaces a physicochemical and engineering aspects,2008. |
APA | Li, Xuejun.,Xiao, Zhiyong.,Lu, Anhuai.,Wang, Lijuan.,Ouyang, Xihui.,...&Li, Yuanyuan.(2008).Preparation and characteristics of NiO-coated nano-fibriform silica.colloids and surfaces a physicochemical and engineering aspects. |
MLA | Li, Xuejun,et al."Preparation and characteristics of NiO-coated nano-fibriform silica".colloids and surfaces a physicochemical and engineering aspects (2008). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论