Adsorption of gaseous iodine-131 at high temperatures by silver impregnated alumina | |
Cheng Qing-Hui ; Li Ze-Jun ; Chu Tai-Wei | |
刊名 | NUCLEAR SCIENCE AND TECHNIQUES
![]() |
2015 | |
关键词 | Silver impregnated alumina High temperature Radioactive iodine Adsorption Decontamination factor RADIOACTIVE METHYL-IODIDE NUCLEAR-POWER-PLANTS ACTIVATED CARBONS REMOVAL WATER SEQUESTRATION ENTRAPMENT NANOFIBERS NANOTUBES CAPTURE |
英文摘要 | To prevent radioactive iodides from releasing into the environment in an accident of a nuclear power plant, silver-impregnated alumina (Ag/Al2O3) was fabricated, and its performance of radioactive iodine adsorption from high-temperature gas was tested. The silver loadings on alumina were obtained by ICP-OES and the texture properties of Ag/Al2O3 were characterized by N-2 adsorption-desorption. The Ag/Al2O3 was of reduced specific surface (107.2 m(2)/g at 650 degrees C). Crystalline phases of Ag/Al2O3 were confirmed through XRD characterization. After calcination at 650 degrees C for 2 h, the crystalline phase of Ag/Al2O3 changed. The I-131-removal efficiency of Ag/Al2O3 was tested at 100, 250, 350, 450 and 650 degrees C, with good decontamination factor values for the radioactive iodine. Silver-impregnated alumina can be applied as adsorbents to remove radioactive iodine at high temperatures in nuclear accident.; SCI(E); 中国科学引文数据库(CSCD); ARTICLE; twchu@pku.edu.cn; 4; 040303-01-040303-05; 26 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/414371] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | Cheng Qing-Hui,Li Ze-Jun,Chu Tai-Wei. Adsorption of gaseous iodine-131 at high temperatures by silver impregnated alumina[J]. NUCLEAR SCIENCE AND TECHNIQUES,2015. |
APA | Cheng Qing-Hui,Li Ze-Jun,&Chu Tai-Wei.(2015).Adsorption of gaseous iodine-131 at high temperatures by silver impregnated alumina.NUCLEAR SCIENCE AND TECHNIQUES. |
MLA | Cheng Qing-Hui,et al."Adsorption of gaseous iodine-131 at high temperatures by silver impregnated alumina".NUCLEAR SCIENCE AND TECHNIQUES (2015). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论