Luminescence and microstructure of Sr2Mg(BO3)(2) doped with Eu | |
Lin, C ; Liu, XR ; Jing, XP ; Liu, YL ; Chen, Y | |
刊名 | 中国稀土学报英文版
![]() |
2005 | |
关键词 | luminescence borate microstructure rare earths RED PHOSPHORS |
英文摘要 | Sr2Mg(BO3)(2) doped with Eu was synthesized respectively in air and weak reducing atmosphere (combustion of carbon particle), whose photoluminescence characteristics and structure were also studied at room-temperature. In air, the fluorescent body's color was white for different synthesized temperatures. At room temperature, the sample was excited and showed red typical emission spectrum of Eu3+ whose emission apex were sharp near 612 mn and emission spectrum was made up of the charge transformation band (CTB) of Eu3+ and excitation spectrum of 4f -> 4f high energy level transition, then reached the area of VUV. However, under reducing atmosphere (combustion of carbon particles), the color of the sample yielded was yellow, whose color became deeper with increasing temperature and showed phase transition. Using UV excitation, the luminescence of yellow sample was very weak. In a complicated broad spectrum at visible light area, the red emission spectrum of Eu2+ was not observed. Crystal structure and luminescence of the sample were completely different from the results of Diaz and Keszler. Two samples were prepared under oxidation and reducing atmosphere at high temperature, which were different on crystal structure and microstructure. By studying Sr2Mg(BO3)(2):Eu3+ a series of directional faults or educts were found, because Eu 3, ions substituted for Sr2+ ions. However, microstructure of Sr2Mg (BO3)(2):Eu2+ is more complicated, whose excitation spectrum might be excited by Eu2+. By XRD patten of the samples, phase transition could be found. Twins and clusters that were formed from point defect such as interstitial atom and big angle crystal boundary could be found by TEM.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000236093300014&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Chemistry, Applied; SCI(E); EI; 中国科技核心期刊(ISTIC); 2; ARTICLE; SUPPL. 3; 48-50; 23 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/399391] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | Lin, C,Liu, XR,Jing, XP,et al. Luminescence and microstructure of Sr2Mg(BO3)(2) doped with Eu[J]. 中国稀土学报英文版,2005. |
APA | Lin, C,Liu, XR,Jing, XP,Liu, YL,&Chen, Y.(2005).Luminescence and microstructure of Sr2Mg(BO3)(2) doped with Eu.中国稀土学报英文版. |
MLA | Lin, C,et al."Luminescence and microstructure of Sr2Mg(BO3)(2) doped with Eu".中国稀土学报英文版 (2005). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论