Quaternary Sulfide Ba6Zn6ZrS14: Synthesis, Crystal Structure, Band Structure, and Multiband Physical Properties | |
Zhang, Xian ; He, Jianqiao ; Chen, Wei ; Zhang, Ketian ; Zheng, Chong ; Sun, Junliang ; Liao, Fuhui ; Lin, Jianhua ; Huang, Fuqiang | |
刊名 | chemistry a european journal
![]() |
2014 | |
关键词 | electronic structure solid-state structures sulfides zinc zirconium TOTAL-ENERGY CALCULATIONS WAVE BASIS-SET ZIRCONIUM SULFIDES BA2ZNS3 PHOSPHOR CLUSTERS ZNS |
DOI | 10.1002/chem.201304525 |
英文摘要 | Ba6Zn6ZrS14 was synthesized by a traditional salt-melt method with KI as flux. The pale yellow crystals of Ba6Zn6ZrS14 crystallize in the tetragonal space group I4/mcm with a=16.3481 (4)angstrom and c=9.7221(6)angstrom. The structure features unique one-dimensional parallel [Zn6S9](6-) and [ZrS5](6-) straight chains. The D-2h-symmetric [Zn6S9](6-) cluster serves as the building block of the [Zn6S9](6-) chains. A powder sample was investigated by X-ray diffraction, optical absorption, and photoluminescence measurements. The compound shows multiple-absorption character with three optical absorption edges around 1.78, 2.50, and 2.65eV, respectively, which are perfectly consistent with the results of first-principles calculations. Analysis of the density of states further revealed that the three optical absorption bands are attributable to the three S(3p(6))Zr(4d(0)) transitions due to the splitting of the Zr 4d orbitals in the D-4h crystal field. The multiband nature of Ba6Zn6ZrS14 also results in photocatalytic activity under visible-light irradiation and three band-edge emissions.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000335433500017&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Chemistry, Multidisciplinary; SCI(E); EI; PubMed; 10; ARTICLE; czheng@niu.edu; jhlin@pku.edu.cn; huangfq@pku.edu.cn; 20; 5977-5982; 20 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/312547] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | Zhang, Xian,He, Jianqiao,Chen, Wei,et al. Quaternary Sulfide Ba6Zn6ZrS14: Synthesis, Crystal Structure, Band Structure, and Multiband Physical Properties[J]. chemistry a european journal,2014. |
APA | Zhang, Xian.,He, Jianqiao.,Chen, Wei.,Zhang, Ketian.,Zheng, Chong.,...&Huang, Fuqiang.(2014).Quaternary Sulfide Ba6Zn6ZrS14: Synthesis, Crystal Structure, Band Structure, and Multiband Physical Properties.chemistry a european journal. |
MLA | Zhang, Xian,et al."Quaternary Sulfide Ba6Zn6ZrS14: Synthesis, Crystal Structure, Band Structure, and Multiband Physical Properties".chemistry a european journal (2014). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论