Preparation and electrochemical properties of unidirectionally solidified Ml(NiCoMnTi)(5) alloys | |
Lei, YQ ; Zhou, Y ; Luo, YC ; Yang, XG ; Wang, QD | |
1997 | |
关键词 | unidirectional solidification mischmetal based alloy microstructure electrochemical properties HYDROGEN STORAGE ALLOYS BATTERIES |
英文摘要 | Mischmetal based alloy Ml(NiCoMnTi)(5) (Ml: La-rich mischmetal) was prepared by unidirectional solidification process at an ultra-high temperature gradient (around 1300 degrees C cm(-1)) and different growth rates (48-220 mu m s(-1)). The microstructures and electrochemical properties of these alloys have been investigated. It was shown that with increasing growth rate, the microstructure of unidirectional solidification alloy changed from cellular-columnar to columnar-dendritic structure and the primary columnar spacing lambda(1) increased, reached a maximum value and then decreased. Electrochemical measurement indicated that unidirectional solidification alloy with the fine cellular-columnar structure prepared at growth rate R=48 mu m s(-1) has significantly improved discharge capacity, high-rate dischargeability and cycling stability of the alloy.; Chemistry, Physical; Materials Science, Multidisciplinary; Metallurgy & Metallurgical Engineering; SCI(E); 15 |
语种 | 英语 |
DOI标识 | 10.1016/S0925-8388(96)02882-4 |
内容类型 | 其他 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/258307] |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | Lei, YQ,Zhou, Y,Luo, YC,et al. Preparation and electrochemical properties of unidirectionally solidified Ml(NiCoMnTi)(5) alloys. 1997-01-01. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论