KInSe2的中温固相合成及结构表征; Solid State Synthesis at Intermediate Temperature and Structural Characterization of KInSe2 | |
王平 ; 黄小荥 ; 刘艳玲 ; 魏永革 ; 李静 ; 郭洪猷 | |
刊名 | 化学学报
![]() |
2000 | |
关键词 | KInSe2 KInSe2 reactive molten salt method solid state synthesis crystal structure 反应性熔盐法 固相合成 晶体结构 |
DOI | 10.3321/j.issn:0567-7351.2000.08.014 |
英文摘要 | 采用反应性熔盐法,以n(K2Se3):n(In):n(Se)=1:1:5的摩尔比,在500℃下反应5d,生成淡黄色柱状晶体KInSe2.该晶体属于单斜晶系,空间群为C2/c,晶胞参数,a=1.1414(2)nm,b=1.1410(2)nm,c=1.5586(3)nm,β=100.60(3)°,Z=16,R=0.0656.KInSe2晶体具有层状结构,每层由具有二维网状结构的[InSe2]-负离子和K+组成,层与层之间按ABAB方式堆积.; A ternary metal selenide KInSe2 has been synthesized by use of the reactive molten salt method. The reactants with molar ratio of n(K2Se3):n(In):n(Se) = 1:1:5 were reacted at 500 degrees C for 5 days. The crystal structure of KInSe2 was determined by X-ray structure analysis. KInSe2 belongs to monoclinic system with space group C2/c. The unit cell parameters are a = 1.1414(2) nm, b = 1.1410(2) nm, c = 1.5586(3) nm, V = 1.9952(6) nm(3), Z = 16. KInSe2 is a layered crystal containing 2D network of (2)(infinity) [InSe2](-) anions and K+ cations. The layers are packed in the sequence ABAB in the crystal. There are two crystallographically independent In atoms, both of which are coordinated to four mu(2) Se atoms to form slight distorted tetrahedra. Of the five crystallographically independent Se atoms, Se(3) and Se(5) are located on 2-fold axes (4e). The K+ ions are six-coordinated to Se.; 国家自然科学基金; 国家重点实验室基金; SCI(E); 中文核心期刊要目总览(PKU); 中国科学引文数据库(CSCD); 5; 8; 1005-1008; 58 |
语种 | 中文 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/257781] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | 王平,黄小荥,刘艳玲,等. KInSe2的中温固相合成及结构表征, Solid State Synthesis at Intermediate Temperature and Structural Characterization of KInSe2[J]. 化学学报,2000. |
APA | 王平,黄小荥,刘艳玲,魏永革,李静,&郭洪猷.(2000).KInSe2的中温固相合成及结构表征.化学学报. |
MLA | 王平,et al."KInSe2的中温固相合成及结构表征".化学学报 (2000). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论