Synthesis, crystal structure and magnetic property of Sm(2-x)Co(x)Ti(2-x)Nb(x)O7 (x=0, 0.2, 0.4) | |
Li, XL ; Song, YW ; Xiong, H ; Jia, YQ ; Matsushita, N ; Xuan, Y | |
刊名 | 材料化学与材料物理学
![]() |
2003 | |
关键词 | pyrochlore compound crystal structure Van Vleck paramagnetism canted ferrimagnet semi-spin glass PYROCHLORE COMPOUNDS OXIDES |
DOI | 10.1016/S0254-0584(01)00587-9 |
英文摘要 | SM2-xCoxTi2-xNbxO7 (X = 0, 0.2, 0.4) were synthesized by a wet chemical method. The compounds possess pyrochlore structure with cubic face-central cell. The lattice parameter (a) is 1.0234 nm for Sm2Ti2O7, 1.0231 nm for Sm1.8Co0.2Ti1.8Nb0.2O7 and 1.0225nm for Sm1.6Co0.4Ti1.6Nb0.4O7. Sm2Ti2O7 may possess the Van Vleck paramagnetism. The variation of the magnetic susceptibility Of Sm2-xCoxTi2-xNbxO7 (X = 0.2, 0.4) with temperature is similar to that of a ferrimagnet in the paramagnetic region. The satisfactory fitting to the experimental plot of the inverse susceptibility of Sm2-xCoxTi2-xNbxO7 (X = 0.2, 0.4) vs. temperature indicates that the compounds may be a canted ferrimagnet. (C) 2002 Elsevier Science B.V. All rights reserved.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000178843700002&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Materials Science, Multidisciplinary; SCI(E); EI; 0; ARTICLE; 3; 625-631; 77 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/256202] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | Li, XL,Song, YW,Xiong, H,et al. Synthesis, crystal structure and magnetic property of Sm(2-x)Co(x)Ti(2-x)Nb(x)O7 (x=0, 0.2, 0.4)[J]. 材料化学与材料物理学,2003. |
APA | Li, XL,Song, YW,Xiong, H,Jia, YQ,Matsushita, N,&Xuan, Y.(2003).Synthesis, crystal structure and magnetic property of Sm(2-x)Co(x)Ti(2-x)Nb(x)O7 (x=0, 0.2, 0.4).材料化学与材料物理学. |
MLA | Li, XL,et al."Synthesis, crystal structure and magnetic property of Sm(2-x)Co(x)Ti(2-x)Nb(x)O7 (x=0, 0.2, 0.4)".材料化学与材料物理学 (2003). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论