Pt纳米线阵列的氧还原催化性能; Catalytic Performance of Pt Nanowire Arrays for Oxygen Reduction | |
张敏 ; 李经建 ; 潘牧 ; 徐东升 | |
刊名 | 物理化学学报
![]() |
2011 | |
关键词 | AAO模板 铂纳米线阵列 氧还原反应 质子交换膜燃料电池 AAO template Platinum nanowire array Oxygen reduction reaction Proton exchange membrane fuel cell |
DOI | 10.3866/PKU.WHXB20110726 |
英文摘要 | 采用阳极氧化铝(AAO)模板法电化学沉积制备了Pt纳米线阵列(Pt NWs)氧还原催化剂,通过扫描电子显微镜(SEM)、透射电子显微镜(TEM)和电化学测试对Pt纳米线阵列催化剂的形貌和电催化性能进行了表征.循环伏安法(CV)研究表明Pt纳和线阵列催化剂的电化学活性面积大于其几何面积;旋转圆盘电极(RDE)测试研究发现,制备的Pt纳米线阵列催化剂的氧还原反应(ORR)曲线的半波电势相对Pt/C的有正移,并且Pt纳米线阵列催化剂的极限扩散电流比Pt/C大.; Platinum nanowire arrays (Pt NWs) catalyst was fabricated by electrodepositing with anodic aluminum oxide (AAO) as a template. The morphology and oxygen reduction reaction (ORR) electrocatalytic properties of the as-prepared platinum nanowire array catalysts were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electrochemical measurements. The cyclic voltammetry (CV) showed that the specific electrochemical surface area (ECSA) of the Pt NWs was much higher than the geometric area. The half wave potential in the oxygen reduction reaction curves of the Pt NWs was more positive than that of Pt/C from the rotating disk electrode (RDE) measurements. Moreover, Pt NWs catalysts give higher limiting diffusion current by comparison with that of conventional Pt/C catalyst.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000292877100020&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; SCI(E); 中文核心期刊要目总览(PKU); 中国科技核心期刊(ISTIC); 中国科学引文数据库(CSCD); 7; 07; 1685-1688; 27 |
语种 | 中文 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/227264] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | 张敏,李经建,潘牧,等. Pt纳米线阵列的氧还原催化性能, Catalytic Performance of Pt Nanowire Arrays for Oxygen Reduction[J]. 物理化学学报,2011. |
APA | 张敏,李经建,潘牧,&徐东升.(2011).Pt纳米线阵列的氧还原催化性能.物理化学学报. |
MLA | 张敏,et al."Pt纳米线阵列的氧还原催化性能".物理化学学报 (2011). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论