	Na掺杂对硅酸锂吸收CO_2性能的影响; Effect of Na-doping on CO2 absorption of Li4SiO4
	王银杰 ; 其鲁 ; 代克化
刊名	物理化学学报
	2006
关键词	硅酸锂吸收掺杂 CO_2 TG lithium silicate absorption carbon dioxide doping TG
DOI	10.3866/PKU.WHXB20060718
英文摘要	通过高温固相反应法,在添加不同比例Na2CO3的条件下,合成出一系列可在高温500～750℃之间直接吸收CO2的硅酸锂材料.利用扫描电子显微镜、X射线粉末衍射仪分别观察和评价了合成材料的表面形貌与结构特征,用热重分析仪测量了硅酸锂材料的CO2吸收性能.实验结果表明,通过适量Na元素的掺杂,能够提高硅酸锂材料吸收CO2的性能,当Na2CO3的添加量x=0.02时,合成的硅酸锂材料在CO2气氛下,于700℃恒温保持约15min即可达到吸收平衡,材料的吸收量为(46±0.6)%(w),与未经掺杂的材料相比,吸收容量有所提高.此外,气氛中CO2的浓度对材料吸收CO2的速率有较大影响.; Sodium-doped lithium silicate as CO2 absorbent at 500C to 750C was prepared by high-temperature solid-state reaction. The influence of sodium doping on the crystal structure of the absorbent was studied by X-ray diffraction (XRD). The microscopic morphologies of the absorbents were observed by scanning electron microscopy (SEM). The CO2-absorption capacities were measured by a thermogravimetric analyzer, which showed that sodium doping could improve the CO2-absorption ability of lithium silicate. It was found that the absorbent possessed the best performance when n(SiO2):n(Li2Co3):n(Na2CO3)=1: 1.96:0.04. The maximum amount of CO2 absorption arrived at (46 0.6)%(w) in CO2 atmosphere at 700 degrees C within 15 min. Moreover, the CO2 concentration in gas phase influenced the rate of CO2 absorption.; SCI(E); 中文核心期刊要目总览(PKU); 中国科技核心期刊(ISTIC); 中国科学引文数据库(CSCD); 0; 07; 860-863; 22
语种	中文
内容类型	期刊论文
源URL	[http://ir.pku.edu.cn/handle/20.500.11897/214803]
专题	化学与分子工程学院
推荐引用方式 GB/T 7714	王银杰,其鲁,代克化. Na掺杂对硅酸锂吸收CO_2性能的影响, Effect of Na-doping on CO2 absorption of Li4SiO4[J]. 物理化学学报,2006.
APA	王银杰,其鲁,&代克化.(2006).Na掺杂对硅酸锂吸收CO_2性能的影响.物理化学学报.
MLA	王银杰,et al."Na掺杂对硅酸锂吸收CO_2性能的影响".物理化学学报 (2006).