KCl熔盐法制备LiMn_2O_4

doi:10.3321/j.issn:1001-4861.2006.05.016

CORC > 北京大学 > 化学与分子工程学院

	KCl熔盐法制备LiMn_2O_4; Synthesis spinel LiMn2O4 in molten KCl
	杜柯 ; 其鲁 ; 胡国荣 ; 彭忠东
刊名	无机化学学报
	2006
关键词	锂离子电池正极材料熔盐法 LiMn_2O_4 lithium-ion battery cathode material LiMn2O4 molten salt synthesis method
DOI	10.3321/j.issn:1001-4861.2006.05.016
英文摘要	采用熔盐法合成了LiMn2O4。熔盐的使用可以使原来固相反应的高温焙烧时间缩短。合成获得的材料结晶良好,颗粒大小在数百个纳米左右,有较明显的团聚现象。该材料的初始容量为113mAh·g-1,循环性能优良,前100次的容量平均衰减率在0.05%左右;倍率性能亦非常优秀,8C放电时的容量为1C放电容量的93%以上。熔盐的用量在4倍于Li+以上时,对材料的结构形貌和性能都没有明显影响。; Sub-micrometer spinel LiMn2O4 was prepared by molten salt Synthesis method, in which molten salt KCl supplies a liquid surrounding for rapid ion reaction at high temperature. By this method, the sintering time could be shortened largely. When assembled as cathode of lithium battery, the LiMn2O4 materials gotten from this new method show good cyclic ability with capacity loss rate about 0.05% during first 100 cycles. And its rate performance is wonderful with the special capacity at 8 C is above 93% of that at 1 C.; SCI(E); 中文核心期刊要目总览(PKU); 中国科技核心期刊(ISTIC); 中国科学引文数据库(CSCD); 2; 05; 867-871; 22
语种	中文
内容类型	期刊论文
源URL	[http://ir.pku.edu.cn/handle/20.500.11897/212257]
专题	化学与分子工程学院
推荐引用方式 GB/T 7714	杜柯,其鲁,胡国荣,等. KCl熔盐法制备LiMn_2O_4, Synthesis spinel LiMn2O4 in molten KCl[J]. 无机化学学报,2006.
APA	杜柯,其鲁,胡国荣,&彭忠东.(2006).KCl熔盐法制备LiMn_2O_4.无机化学学报.
MLA	杜柯,et al."KCl熔盐法制备LiMn_2O_4".无机化学学报 (2006).