Interfacial growth behavior of SnO2 nanorods on {1120} and {1010} facets of ��-Fe2O3 | |
Zhang, Yi-Qun ; Sun, Ling-Dong ; Feng, Wei ; Wu, Hao-Shuai ; Yan, Chun-Hua | |
刊名 | nanoscale
![]() |
2012 | |
DOI | 10.1039/c2nr31177a |
英文摘要 | SnO2 nanorods with specific growth directions, [101] or [001], were fabricated on ??-Fe2O3 substrates via a simple hydrothermal method. The growth behavior of SnO2 nanorods is facet-selective. Both {1120} and {1010} facets of ??-Fe2O 3 are favorable to direct the growth of SnO2 nanorods. The correlation between the crystallographic orientation of SnO2 and the facets of ??-Fe2O3 is characterized by TEM observations and investigated on the basis of the interfacial lattice compatibility. Furthermore, the distribution and coordination of oxygen atoms at the interface of ??-Fe2O3-SnO2 heterostructure are analyzed, which reveals that only slight deviations from their original equilibrium positions are allowed for the formation of heterogeneous interface. And this lower energy activated interfacial construction is beneficial to the feasibility and stability of heterostructures. ? 2012 The Royal Society of Chemistry.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000306855500036&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; SCI(E); EI; PubMed; 7; ARTICLE; 16; 5092-5097; 4 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/191058] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | Zhang, Yi-Qun,Sun, Ling-Dong,Feng, Wei,et al. Interfacial growth behavior of SnO2 nanorods on {1120} and {1010} facets of ��-Fe2O3[J]. nanoscale,2012. |
APA | Zhang, Yi-Qun,Sun, Ling-Dong,Feng, Wei,Wu, Hao-Shuai,&Yan, Chun-Hua.(2012).Interfacial growth behavior of SnO2 nanorods on {1120} and {1010} facets of ��-Fe2O3.nanoscale. |
MLA | Zhang, Yi-Qun,et al."Interfacial growth behavior of SnO2 nanorods on {1120} and {1010} facets of ��-Fe2O3".nanoscale (2012). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论