Synthesis, Structure, Multiband Optical, and Electrical Conductive Properties of a 3D Open Cubic Framework Based on [Cu8Sn6S24](z-) Clusters | |
Zhang Xian ; Wang Qiuran ; Ma Zhimin ; He Jianqiao ; Wang Zhe ; Zheng Chong ; Lin Jianhua ; Huang Fuqiang | |
刊名 | inorganic chemistry |
2015 | |
DOI | 10.1021/acs.inorgchem.5b00317 |
英文摘要 | Two compounds with the formulas of Na4Cu32Sn12S48·4H2O and K11Cu32Sn12S48·4H2O were synthesized via flux (with thiourea as reactive flux) and hydrothermal method, respectively. The black crystals of Na4Cu32Sn12S48·4H2O and K11Cu32Sn12S48·4H2O both crystallize in the cubic space group of Fm3?c with the cell constants a = 17.921(2) ? and a = 18.0559(6) ?, respectively. The crystal structures feature a 3D open-framework with the unique [Cu8Sn6S24](z-) (z = 13 for Na4Cu32Sn12S48·4H2O; z = 14.75 for K11Cu32Sn12S48·4H2O) clusters acting as building blocks. The [Cu8Sn6S24](z-) cluster of the Th symmetry is built up by eight [CuS3] triangles and six [SnS4] tetrahedra. The powder samples were investigated by X-ray diffraction and optical absorption measurements. Both phase-pure compounds show multiabsorption character with a main absorption edge (2.0 eV for Na4Cu32Sn12S48·4H2O and 1.9 eV for K11Cu32Sn12S48·4H2O) and an additional absorption peak (1.61 eV for Na4Cu32Sn12S48·4H2O and 1.52 eV for K11Cu32Sn12S48·4H2O), which are perfectly consistent with the first-principle calculation results. The analyses of the density of states further reveal that the two optical absorption bands in each compound are attributed to the two transitions of Cu-3d-S-3p → Sn-5s. The multiband nature of two compounds also enhances photocatalytic activity under visible light irradiation, with which the degradation of methyl blue over Na4Cu32Sn12S48·4H2O reached 100% in 3 h. The 3D open-framework features also facilitate the ionic conductivity nature of the Na4Cu32Sn12S48·4H2O compound, which achieved ~10(-5) S/cm at room temperature.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000355638100035&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; SCI(E); PubMed; 5; ARTICLE; huangfq@pku.edu.cn |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/187957] |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | Zhang Xian,Wang Qiuran,Ma Zhimin,et al. Synthesis, Structure, Multiband Optical, and Electrical Conductive Properties of a 3D Open Cubic Framework Based on [Cu8Sn6S24](z-) Clusters[J]. inorganic chemistry,2015. |
APA | Zhang Xian.,Wang Qiuran.,Ma Zhimin.,He Jianqiao.,Wang Zhe.,...&Huang Fuqiang.(2015).Synthesis, Structure, Multiband Optical, and Electrical Conductive Properties of a 3D Open Cubic Framework Based on [Cu8Sn6S24](z-) Clusters.inorganic chemistry. |
MLA | Zhang Xian,et al."Synthesis, Structure, Multiband Optical, and Electrical Conductive Properties of a 3D Open Cubic Framework Based on [Cu8Sn6S24](z-) Clusters".inorganic chemistry (2015). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论