YAG:Ce蓝光转换材料的合成和发光性质研究

doi:10.3321/j.issn:1000-7032.2001.z1.006

CORC > 北京大学 > 化学与分子工程学院

	YAG:Ce蓝光转换材料的合成和发光性质研究; Preparation and Luminescence of Blue Light Conversion Material YAG: Ce
	姚光庆 ; 段洁菲 ; 任敏 ; 于海东 ; 林建华
刊名	发光学报
	2001
关键词	YAG:Ce 蓝光转换材料白光
DOI	10.3321/j.issn:1000-7032.2001.z1.006
英文摘要	铈激活的钇铝石榴石(YAG:Ce)由高温固相反应制备.样品证明为纯的的石榴石物相.YAG:Ce的激发光谱为双峰结构,主要激发峰在460nm,与GaN的蓝光发射匹配.YAG:Ce的发射光谱为一宽带,波长范围从蓝绿到红,主峰波长为540nm,能与GaN的蓝光组合形成高亮度白光.YAG:Ce在漫反射光谱中的的两个吸收峰与YAG:Ce的激发峰相吻合,进一步证明了铈激活的YAG对GaN蓝光的有效吸收.YAG:Ce有很高的发光强度和高达89%的量子效率.; Yttrium aluminum garnet doped by cerium (YAG: Ce), is prepared by high temperature solid reaction. Its absorption band has two peaks. The major one is around 460nm, which matches the blue emission of GaN LED very well. Its emission band is wide, from blue to red.The emission peak is at 540nm, which can combine the blue light of GaN LED to yield bright white light. The wavelength of two peaks of the diffusion spectrum is similar to that of the excitation spectrum. That indicates the YAG: Ce has effective absorption for blue light of GaN.YAG: Ce phosphor has strong emission intensity, and the quantum efficecy is 89%.; 国家高技术研究发展计划(863计划); 中文核心期刊要目总览(PKU); 中国科学引文数据库(CSCD); 0; z1; 21-23; 22
语种	中文
内容类型	期刊论文
源URL	[http://ir.pku.edu.cn/handle/20.500.11897/83057]
专题	化学与分子工程学院
推荐引用方式 GB/T 7714	姚光庆,段洁菲,任敏,等. YAG:Ce蓝光转换材料的合成和发光性质研究, Preparation and Luminescence of Blue Light Conversion Material YAG: Ce[J]. 发光学报,2001.
APA	姚光庆,段洁菲,任敏,于海东,&林建华.(2001).YAG:Ce蓝光转换材料的合成和发光性质研究.发光学报.
MLA	姚光庆,et al."YAG:Ce蓝光转换材料的合成和发光性质研究".发光学报 (2001).