氧化锡基甲烷催化燃烧催化剂的硫中毒反应机理; Sulphur poisoning mechanism of SnO2 based catalysts for methane combustion | |
周长军 ; 林伟 ; 朱月香 ; 谢有畅 | |
2003 | |
关键词 | 硫中毒 甲烷燃烧 氧化锡 sulphur poisoning methane combustion tin dioxide |
英文摘要 | 测定了几种活性较高的氧化锡基甲烷燃烧催化剂在200×10-6(φ)SO2存在下的催化活性.结果发现,SnCrO样品具有很好的抗硫性能,而SnCuO及SnCoO样品在SO2存在时的活性大大降低.用XRD、BET、XPS、FT-IR及DTA-TG等技术对反应前后的样品进行了表征,结果表明,硫酸盐的热稳定性对催化剂在SO2处理过程中的变化起决定作用.在实验的温度下(500℃),Co2(SO4)3和CuSO4均能稳定存在,而Cr2(SO4)3会分解.SnCrO样品在SO2存在下反应时只是表面吸附少量硫酸根,因此其催化活性基本保持不变.这是SnCrO样品具有良好抗硫性能的原因.; The catalytic activity of several SnO2 based catalysts for methane combustion in the presence of 200 x 10(-6)( phi, volume fraction) SO2 were tested. The results showed that among these samples studied SnCrO possessed the highest resistance to sulphur poisoning, while the catalytic activity of SnCuO and SnCoO samples decreased significantly. XRD, BET, XPS, FT-IR and DTA-TG techniques were employed to characterize the samples before and after reaction in SO2, and it was found that the thermal stability of the respective metal sulfates played an important role in the combustions of methane in the presence of SO2. At 500 degreesC, CO2(SO4)(3) and CuSO4 are stable but Cr-2 (SO4)(3) can decompose, therefore, during the reaction in 200 x 10(-6)(phi) SO2, SnCrO sample only adsorbs a small amount of SO42- ions on its surface and the activity remains almost unchanged, which is the reason for the highest resistance of SnCrO sample to sulphur poisoning.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000181749700013&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; SCI(E); 中文核心期刊要目总览(PKU); 中国科技核心期刊(ISTIC); 中国科学引文数据库(CSCD); 2; 03; 246-250; 19 |
语种 | 中文 |
出处 | 万方 ; 知网 ; SCI |
出版者 | 物理化学学报 |
内容类型 | 其他 |
源URL | [http://hdl.handle.net/20.500.11897/80666] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | 周长军,林伟,朱月香,等. 氧化锡基甲烷催化燃烧催化剂的硫中毒反应机理, Sulphur poisoning mechanism of SnO2 based catalysts for methane combustion. 2003-01-01. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论