GaAs基底上金纳米粒子的二维组装及其表面增强喇曼散射活性; Self-assembled Au Nanoparticles on GaAs and Its Surface Enhanced Raman Scattering(SERS)-activity | |
陈海峰 ; 王健 ; 蔡生民 ; 刘忠范 | |
1999 | |
关键词 | GaAs GaAs gold nanoparticle self-assembled SERS 金纳米粒子 组装 表面增强喇曼散射 |
英文摘要 | 利用巯基苯胺作耦联分子,成功地将Au纳米粒子组装到GaAs(100)表面上,并且用TM-AFM观察了纳米粒子在表面上的分布情况.Raman研究表明,该基底显示出表面增强喇曼散射活性.; By using p-aminothiophenol(PATP) as the coupling molecular, the Au nanoparticles were successfully self-assembled onto the GaAs(100) surface. Firstly, the mechanically polished semi-insulating GaAs(100) wafers were degreased in trichloroethylene, acetone, methanol, and the surface oxides were chemically polished and removed by rinsing them in V(H2SO4) : V (H2O2) : V(H2O) = 3 : 1 : 1, V(NH4OH) : V(H2O2) : V(H2O) = 1 : 1 : 7, HCl and de-ionized water. Then the wafers were dried with argon and immediately immersed in 1 mmol/L ethanol solution of PATP. After assembling in the solution for 24 h with argon protection, the GaAs(100) wafers with PATP SAMs were ultrasonicated in pure ethanol to remove those physical adsorbed PATP molecules. Assembling of gold nanoparticles (70 nm) were handled by immersing thus prepared GaAs(100) wafers with PATP SAMs in a colloidal gold suspension for 6 h. The gold nanoparticles were scattered over such a surface. Thus the prepared samples showed a surface enhanced Raman scattering(SERS)-activity.; 国家攀登计划; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000079767600031&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; SCI(E); 中文核心期刊要目总览(PKU); 中国科学引文数据库(CSCD); 12; 4; 620-623; 20 |
语种 | 中文 |
出处 | 万方 ; SCI ; http://d.g.wanfangdata.com.cn/Periodical_gdxxhxxb199904021.aspx |
出版者 | 高等学校化学学报 |
内容类型 | 其他 |
源URL | [http://hdl.handle.net/20.500.11897/78542] ![]() |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | 陈海峰,王健,蔡生民,等. GaAs基底上金纳米粒子的二维组装及其表面增强喇曼散射活性, Self-assembled Au Nanoparticles on GaAs and Its Surface Enhanced Raman Scattering(SERS)-activity. 1999-01-01. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论