Fatigue damage and fracture behavior of metallic glass under cyclic compression | |
Wang, XD; Qu, RT; Wu, SJ; Liu, ZQ; Zhang, ZF; Zhang, ZF (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China. | |
刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING |
2018-02-21 | |
卷号 | 717页码:41-47 |
关键词 | Crack-growth-behavior Shear-band Propagation Dynamics Simulations Strength Mechanism Evolution Endurance Failure Alloys Steels |
ISSN号 | 0921-5093 |
英文摘要 | A comprehensive understanding on the fatigue behavior of metallic glasses (MGs) is of vital importance for their structural applications. Here we present a systematic study on the fatigue damage and fracture behavior of. a Zr52.5Cu17.9Ni14.6Al10Ti5 MG under cyclic compression of different stress levels, with the assistance of 3D X-ray tomography (XRT) and 2D scanning electron microscope to examine the origins of fatigue cracks. The results indicate that the fatigue fracture mode of the MG depends strongly on the stress level in such a manner similar to that of high-strength steels. The MG exhibits shear fracture along shear band under high cyclic stress level, just like the case for monotonic compression; under low cyclic stress level, in contrast, the fracture is dominated by splitting where the fatigue cracks originate from extrinsic defects. The increased propensity for cavitation and cracking under low stress level, as revealed by XRT, suggests a reduced resistance of the MG to cleavage failure which eventually leads to the transition of the fatigue fracture mode. The results support the idea that the fatigue performance of MGs can be improyed by reducing the extrinsic defects and properly controlling the shear banding behavior.; A comprehensive understanding on the fatigue behavior of metallic glasses (MGs) is of vital importance for their structural applications. Here we present a systematic study on the fatigue damage and fracture behavior of. a Zr52.5Cu17.9Ni14.6Al10Ti5 MG under cyclic compression of different stress levels, with the assistance of 3D X-ray tomography (XRT) and 2D scanning electron microscope to examine the origins of fatigue cracks. The results indicate that the fatigue fracture mode of the MG depends strongly on the stress level in such a manner similar to that of high-strength steels. The MG exhibits shear fracture along shear band under high cyclic stress level, just like the case for monotonic compression; under low cyclic stress level, in contrast, the fracture is dominated by splitting where the fatigue cracks originate from extrinsic defects. The increased propensity for cavitation and cracking under low stress level, as revealed by XRT, suggests a reduced resistance of the MG to cleavage failure which eventually leads to the transition of the fatigue fracture mode. The results support the idea that the fatigue performance of MGs can be improyed by reducing the extrinsic defects and properly controlling the shear banding behavior. |
学科主题 | Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
资助机构 | National Natural Science Foundation of China (NSFC) [51771205, 51331007, 51501190] |
公开日期 | 2018-06-05 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/79491] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Qu, RT; Zhang, ZF (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China. |
推荐引用方式 GB/T 7714 | Wang, XD,Qu, RT,Wu, SJ,et al. Fatigue damage and fracture behavior of metallic glass under cyclic compression[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2018,717:41-47. |
APA | Wang, XD,Qu, RT,Wu, SJ,Liu, ZQ,Zhang, ZF,&Zhang, ZF .(2018).Fatigue damage and fracture behavior of metallic glass under cyclic compression.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,717,41-47. |
MLA | Wang, XD,et al."Fatigue damage and fracture behavior of metallic glass under cyclic compression".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 717(2018):41-47. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论