Influence of sealing treatment on the corrosion behavior of HVAF sprayed Al-based amorphous/nanocrystalline coating | |
Zhang, LM; Zhang, SD; Ma, AL; Hu, HX; Zheng, YG; Yang, BJ; Wang, JQ | |
刊名 | SURFACE & COATINGS TECHNOLOGY |
2018-11-15 | |
卷号 | 353页码:263-273 |
关键词 | Al-based amorphous/nanocrystalline coating Sealing treatment Polarization EIS XPS Corrosion resistance |
ISSN号 | 0257-8972 |
DOI | 10.1016/j.surfcoat.2018.08.086 |
英文摘要 | Al-based amorphous/nanocrystalline coating with a low porosity (0.42%) and a high amorphous content (80.3%) was fabricated by high velocity air-fuel spraying on aluminum alloy 2024. This thin amorphous/nanocrystalline coating with alpha-Al nanocrystals precipitated in amorphous matrix displays good short-term corrosion resistance, while the corrosion resistance decreases rapidly with increased immersion time. Sealing treatment can effectively close the connecting pores and reduce the porosity defects of coating, thereby improving the corrosion resistance. Among the three selected sealants, stearic acid exhibits the best sealing effect on Al-based amorphous/nanocrystalline coating due to its good impermeability and hydrophobicity, followed by potassium dichromate and nickel acetate. The sealing mechanisms of the three sealants are discussed in terms of reactions at the coating/sealant interface and hydrophobicity of stearic acid. |
学科主题 | Materials Science, Coatings & Films ; Physics, Applied |
语种 | 英语 |
WOS记录号 | WOS:000447117400030 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/79823] |
专题 | 金属研究所_中国科学院金属研究所 |
作者单位 | 1.[Zhang, L. M. 2.Ma, A. L. 3.Hu, H. X. 4.Zheng, Y. G.] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, 62 Wencui Rd, Shenyang 110016, Liaoning, Peoples R China 5.[Zhang, L. M.] Univ Sci & Technol China, Sch Mat Sci & Engn, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China 6.[Zhang, S. D. 7.Yang, B. J. 8.Wang, J. Q.] Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, LM,Zhang, SD,Ma, AL,et al. Influence of sealing treatment on the corrosion behavior of HVAF sprayed Al-based amorphous/nanocrystalline coating[J]. SURFACE & COATINGS TECHNOLOGY,2018,353:263-273. |
APA | Zhang, LM.,Zhang, SD.,Ma, AL.,Hu, HX.,Zheng, YG.,...&Wang, JQ.(2018).Influence of sealing treatment on the corrosion behavior of HVAF sprayed Al-based amorphous/nanocrystalline coating.SURFACE & COATINGS TECHNOLOGY,353,263-273. |
MLA | Zhang, LM,et al."Influence of sealing treatment on the corrosion behavior of HVAF sprayed Al-based amorphous/nanocrystalline coating".SURFACE & COATINGS TECHNOLOGY 353(2018):263-273. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论