Fabrication and mechanical properties of h-BN based composites containing dual glass phases | |
Chen, JJ; Chen, JX; Zhang, X2; Hu, MM; Li, MS | |
刊名 | JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
![]() |
2018-08-01 | |
卷号 | 38期号:9页码:3210-3216 |
关键词 | h-BN Dual glass phases Vitrification Coordination state Strengthening |
ISSN号 | 0955-2219 |
DOI | 10.1016/j.jeurceramsoc.2018.02.035 |
英文摘要 | In this work, h-BN based composites containing amorphous silica and ytterbium silicate glass phases were successfully fabricated by in situ hot pressing process. The powder mixtures of h-BN, Yb2O3, SiO2 and sintering additive (Al2O3) were hot pressed at 1880 C for 1 h under 30 MPa in Ar atmosphere. In the composites, beta-Yb2Si2O7 phase produced from the reaction between Yb2O3 and SiO2 disappears completely and transforms to Yb-Si-Al-O glass when the amount of Al2O3 is >= 15 wt.%. The Vickers hardness, flexural strength, and compressive strength reached the maximum values of 2.38 +/- 0.08 GPa, 337 +/- 22 MPa and 950 +/- 34 MPa, respectively, as 1.5 wt.% Al2O3 was added. The strengthening effects were attributed to the fine spherical microstructure of Yb-Si-Al-O glass particles, strong [AlO4] coordination state, and residual compressive stress in glass phases. |
学科主题 | Materials Science, Ceramics |
语种 | 英语 |
WOS记录号 | WOS:000433014200020 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/80082] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
作者单位 | 1.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, High Performance Ceram Div, Shenyang 110016, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.Xian Golden Mt Ceram Composites Co Ltd, Xian 710065, Shaanxi, Peoples R China |
推荐引用方式 GB/T 7714 | Chen, JJ,Chen, JX,Zhang, X,et al. Fabrication and mechanical properties of h-BN based composites containing dual glass phases[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,2018,38(9):3210-3216. |
APA | Chen, JJ,Chen, JX,Zhang, X,Hu, MM,&Li, MS.(2018).Fabrication and mechanical properties of h-BN based composites containing dual glass phases.JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,38(9),3210-3216. |
MLA | Chen, JJ,et al."Fabrication and mechanical properties of h-BN based composites containing dual glass phases".JOURNAL OF THE EUROPEAN CERAMIC SOCIETY 38.9(2018):3210-3216. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论