Radial X-ray diffraction study of the static strength and texture of tungsten to 96 GPa
Liu, J; Bai LG(白利刚); Li XD(李晓东); Liu J(刘景); Tang, YM; Li, B; Xiong, L; Li, Q; Hao, JB; Bai, LG
刊名SOLID STATE COMMUNICATIONS
2018
卷号269页码:83-89
关键词W High pressure Strength Texture Radial X-ray diffraction DAC
ISSN号0038-1098
DOI10.1016/j.ssc.2017.10.016
文献子类Article
英文摘要Investigations of equation of state, strength and texture of tungsten (W) have been performed under non hydrostatic compression up to 96 GPa using an angle-dispersive radial X-ray diffraction (RXRD) techniques together with the lattice strain theory in a 2-fold paranomic diamond anvil cell (DAC) at ambient temperature. The ratio of t/G is found to remain constant above similar to 35 GPa, indicating that the W started to experience macro yield with plastic deformation at this pressure. Combined with independent constraints on the high-pressure shear modulus, we found that W sample could support a differential stress of similar to 4.57 GPa when it started to yield with plastic deformation at similar to 35 GPa under uniaxial compression. The differential stress in W ranges from 0.01 GPa to 1.46 GPa with pressure increasing from 6 GPa to 35 GPa and can be described as t = -0.904(136) + 0.154(6)P, where P is the pressure in GPa. A maximum differential stress, as high as similar to 6.46 GPa can be supported by W at the highest pressure of similar to 96 GPa. In addition, we have investigated the texture of W under nonhydrostatic compression up to the highest pressure of 96 GPa using the software package MAUD (Material Analysis Using Diffraction). It is convinced that the plastic deformation due to stress under high pressures is responsible for the development of texture.
电子版国际标准刊号1879-2766
WOS关键词SHEAR-STRENGTH ; HIGH-PRESSURE ; LATTICE STRAINS ; COMPRESSION ; CALIBRATION ; MOLYBDENUM ; METALS ; GAUGE ; IRON ; MBAR
WOS研究方向Physics
语种英语
WOS记录号WOS:000418276700016
内容类型期刊论文
源URL[http://ir.ihep.ac.cn/handle/311005/285507]  
专题高能物理研究所_多学科研究中心
作者单位中国科学院高能物理研究所
推荐引用方式
GB/T 7714
Liu, J,Bai LG,Li XD,et al. Radial X-ray diffraction study of the static strength and texture of tungsten to 96 GPa[J]. SOLID STATE COMMUNICATIONS,2018,269:83-89.
APA Liu, J.,白利刚.,李晓东.,刘景.,Tang, YM.,...&Li, XD.(2018).Radial X-ray diffraction study of the static strength and texture of tungsten to 96 GPa.SOLID STATE COMMUNICATIONS,269,83-89.
MLA Liu, J,et al."Radial X-ray diffraction study of the static strength and texture of tungsten to 96 GPa".SOLID STATE COMMUNICATIONS 269(2018):83-89.
个性服务
查看访问统计
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。


©版权所有 ©2017 CSpace - Powered by CSpace