	Crystal morphology of phenyl-capped tetraaniline in the leucoemeraldine oxidation state
	Zhou, YC ; Geng, JX ; Chen, JF ; Gao, L ; Zhou, EL ; Liang, C ; Zhang, WJ
刊名	CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE
	2003-12-01
卷号	24 期号:12 页码:2300-2303
关键词	Tetraaniline Tem Crystal Morphology Crystal Size
ISSN号	0251-0790
英文摘要	A series of crystals of phenyl-capped tetraaniline in the leucoemeraldine oxidation state were obtained with three different preparation methods and were observed directly under transmission electron microscope (TEM). The crystals that crystallized at a higher temperature have a more perfect structure than those at a lower temperature. Both the lamella thickness and the crystal size increase as the isothermal temperatures increase. The oligomer is apt to form a larger scale crystal under a low degree of supercooling. Additionally, the crystal morphology has an important relationship with the kind of substrate on which the oligomer grows, and it will also change with the variation of solvents in which tetraaniline dissolves.
语种	英语
出版者	HIGHER EDUCATION PRESS
WOS记录号	WOS:000187660500043
内容类型	期刊论文
源URL	[http://ir.iccas.ac.cn/handle/121111/80903]
专题	中国科学院化学研究所
通讯作者	Gao, L
作者单位	1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 2.Jilin Univ, Alan G MacDiarmid Inst, Changchun 130012, Peoples R China
推荐引用方式 GB/T 7714	Zhou, YC,Geng, JX,Chen, JF,et al. Crystal morphology of phenyl-capped tetraaniline in the leucoemeraldine oxidation state[J]. CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE,2003,24(12):2300-2303.
APA	Zhou, YC.,Geng, JX.,Chen, JF.,Gao, L.,Zhou, EL.,...&Zhang, WJ.(2003).Crystal morphology of phenyl-capped tetraaniline in the leucoemeraldine oxidation state.CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE,24(12),2300-2303.
MLA	Zhou, YC,et al."Crystal morphology of phenyl-capped tetraaniline in the leucoemeraldine oxidation state".CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE 24.12(2003):2300-2303.