Synthesis and morphological structure of crystalline syndiotactic 1,2-polybutadiene | |
Chen, Y; Yang, DC; Hu, YM; Zhang, XQ | |
刊名 | CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE
![]() |
2003-11-01 | |
卷号 | 24期号:11页码:2119-2121 |
关键词 | Synthesis Morphological Structure Transmission Electron Microscopy Syndiotactic 1 2-polybutadiene |
ISSN号 | 0251-0790 |
英文摘要 | The crystalline syndiotactic 1,2-polybutadiene was synthesized in a catalytic system consisting of iron acetylacetonate [Fe(acac)3], triisobutylaluminum [Al(i-Bu)(3)] and diethyl phosphite (DEP), and its morphological structure was investigated by transmission electron microscopy (TEM). The polymer with a melting point 179 degreesC was found to have 89.3% 1,2 polybutadiene and 86.5% syndiotacticity based on C-13 NMR measurements. The bright field electron micrograph shows that the solution cast film of syndiotactic 1, 2-polybutadiene consists of lamellae with lateral scale in micron size. It should be noted that the lamellae have no branching and they are almost parallel each other in localized areas. The lamellar growing direction is along b axis. Surprisingly, the electron diffraction pattern of the film only exhibits strong (hko) reflections, which indicate that the lamellae possess a single crystal-like orientation, i. e., with their c axis perpendicular to the film plane, while a and b axes in the film plane. According to the orthorhombic packing of plane zigzag chains, the cell parameters calculated from the electron diffraction pattern are a=1. 102 nm, b=0.664 nm, respectively, which are completely consistent with the results reported by Natta et al. |
语种 | 英语 |
出版者 | HIGHER EDUCATION PRESS |
WOS记录号 | WOS:000186799000051 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/80727] ![]() |
专题 | 中国科学院化学研究所 |
通讯作者 | Yang, DC |
作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 2.Chinese Acad Sci, Changchun Inst Appl Chem, Polymer Engn Lab, Changchun 130022, Peoples R China |
推荐引用方式 GB/T 7714 | Chen, Y,Yang, DC,Hu, YM,et al. Synthesis and morphological structure of crystalline syndiotactic 1,2-polybutadiene[J]. CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE,2003,24(11):2119-2121. |
APA | Chen, Y,Yang, DC,Hu, YM,&Zhang, XQ.(2003).Synthesis and morphological structure of crystalline syndiotactic 1,2-polybutadiene.CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE,24(11),2119-2121. |
MLA | Chen, Y,et al."Synthesis and morphological structure of crystalline syndiotactic 1,2-polybutadiene".CHEMICAL JOURNAL OF CHINESE UNIVERSITIES-CHINESE 24.11(2003):2119-2121. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论