Effects of rubber content and temperature on unstable fracture behavior in ABS materials with different particle sizes | |
Han, Y; Lach, R; Grellmann, W | |
刊名 | JOURNAL OF APPLIED POLYMER SCIENCE
![]() |
2001-01-03 | |
卷号 | 79期号:1页码:9-20 |
关键词 | Antibodies Instrumented Charpy Impact Test J-integral Value Plastic Zone Unstable Crack Propagation Brittle-to-tough Transition Crack Opening Displacement |
ISSN号 | 0021-8995 |
英文摘要 | The fracture behavior of ABS materials with a particle diameter of 110 nm and of 330 nm was studied using instrumented Charpy impact tests. The effects of rubber content and temperature on fracture behavior, deformation mode, stable crack extension, plastic zone size, J-integral value, and crack opening displacement were investigated. In the case of a particle size of 110 nm, the material was found to break in a brittle manner, and the dominant crack mechanism was unstable crack propagation. Fracture toughness increases with increasing rubber content. In the case of a particle size of 330 nm, brittle-to-tough transition was observed. The J-integral value first increases with rubber content, then levels off after the rubber content is greater than 16 wt %. The J-integral value of a particle diameter of 330 nm was found to be much greater than that of 110 nm. The J-integral value of both series first increased with increasing temperature until reaching the maximum value, after which it decreased with further increasing temperature. The conclusion is that a particle diameter of 330 nm is more efficient than that of 110 nm in toughening, but for both series the effectiveness of rubber modification decreases with increasing temperatures higher than 40 degreesC because of intrinsic craze formation in the SAN matrix at temperatures near the glass transition of SAN. (C) 2000 John Wiley & Sons, Inc. |
语种 | 英语 |
出版者 | JOHN WILEY & SONS INC |
WOS记录号 | WOS:000165602600002 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/77999] ![]() |
专题 | 中国科学院化学研究所 |
通讯作者 | Han, Y |
作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 2.Univ Halle Wittenberg, Dept Mat Sci, D-06099 Halle, Saale, Germany |
推荐引用方式 GB/T 7714 | Han, Y,Lach, R,Grellmann, W. Effects of rubber content and temperature on unstable fracture behavior in ABS materials with different particle sizes[J]. JOURNAL OF APPLIED POLYMER SCIENCE,2001,79(1):9-20. |
APA | Han, Y,Lach, R,&Grellmann, W.(2001).Effects of rubber content and temperature on unstable fracture behavior in ABS materials with different particle sizes.JOURNAL OF APPLIED POLYMER SCIENCE,79(1),9-20. |
MLA | Han, Y,et al."Effects of rubber content and temperature on unstable fracture behavior in ABS materials with different particle sizes".JOURNAL OF APPLIED POLYMER SCIENCE 79.1(2001):9-20. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论