alpha-Fe2O3 Nanostructures: Inorganic Salt-Controlled Synthesis and Their Electrochemical Performance toward Lithium Storage | |
Wu, Xing-Long2; Guo, Yu-Guo1; Wan, Li-Jun1; Hu, Chang-Wen | |
刊名 | JOURNAL OF PHYSICAL CHEMISTRY C |
2008-10-30 | |
卷号 | 112期号:43页码:16824-16829 |
ISSN号 | 1932-7447 |
DOI | 10.1021/jp8058307 |
英文摘要 | By applying the concept of an inorganic structure-directing agent, uniform alpha-Fe2O3 nanospheres of about 300 nm in diameter and well-defined nanorhombohedra of about 50-80 nm in size have been successfully synthesized using the simple inorganic sodium salt of NaAc and NaCl as the only structure-directing agent in the hydrothermal system, respectively. In comparison, only micrometer sphere-like aggregates composed of irregular nanoparticles of about 80-120 nm were obtained without the presence of any inorganic salt additives. All three nanostructures are investigated with XRD, SEM, TEM, and electrochemical tests toward lithium storage. It is found that the particle size and shape hits a remarkable effect on the lithium insertion/extraction behavior. Among the three alpha-Fe2O3 nanostructures, nanospheres show a very high specific capacity of >600 mA h g(-1) in the initial 10 cycles and >414 mA h g(-1) after 60 cycles as well as good cycling performance, exhibiting great potential as anode materials in lithium-ion batteries. It benefits from the proper submicrometer size with the right surface area and the spherical shape. |
语种 | 英语 |
出版者 | AMER CHEMICAL SOC |
WOS记录号 | WOS:000260357800017 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/65711] |
专题 | 中国科学院化学研究所 |
通讯作者 | Guo, Yu-Guo |
作者单位 | 1.Chinese Acad Sci, Inst Chem, Key Lab Mol Nanostruct & Nanotechnol, Beijing 100190, Peoples R China 2.CAS, Grad Sch, Beijing 100064, Peoples R China 3.BNLMS, Beijing 100190, Peoples R China |
推荐引用方式 GB/T 7714 | Wu, Xing-Long,Guo, Yu-Guo,Wan, Li-Jun,et al. alpha-Fe2O3 Nanostructures: Inorganic Salt-Controlled Synthesis and Their Electrochemical Performance toward Lithium Storage[J]. JOURNAL OF PHYSICAL CHEMISTRY C,2008,112(43):16824-16829. |
APA | Wu, Xing-Long,Guo, Yu-Guo,Wan, Li-Jun,&Hu, Chang-Wen.(2008).alpha-Fe2O3 Nanostructures: Inorganic Salt-Controlled Synthesis and Their Electrochemical Performance toward Lithium Storage.JOURNAL OF PHYSICAL CHEMISTRY C,112(43),16824-16829. |
MLA | Wu, Xing-Long,et al."alpha-Fe2O3 Nanostructures: Inorganic Salt-Controlled Synthesis and Their Electrochemical Performance toward Lithium Storage".JOURNAL OF PHYSICAL CHEMISTRY C 112.43(2008):16824-16829. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论