Near infrared electrochromism of lutetium phthalocyanine | |
Zhang, DJ; Lu, FL; Huang, HC; Wang, J; Yu, H; Jiang, JZ; Yan, DH; Wang, ZY | |
刊名 | SYNTHETIC METALS |
2005-01-31 | |
卷号 | 148期号:2页码:123-126 |
关键词 | Lutetium Phthalocyanine Near Infrared Electrochromism |
ISSN号 | 0379-6779 |
DOI | 10.1016/j.synthmet.2004.09.027 |
英文摘要 | The near infrared (NIR) electrochromism of lutetium phthalocyanine (LuPc2) is studied both in its solution and vacuum deposited thin film. The LuPc2 in neutral state has near infrared absorption in the region from 1100 nm to 1600 nm. In electrochemical oxidized state (+1.0 V), it has an absorption peak at 880 nm. In electrochemical reduced state (-1.0 V), it shows no absorption in the near IR region. The attenuation at 1300 nm of electrochromic (EC) devices based on solution and thin film of LuPC2 was also studied. Attenuation of 0.31 dB and 0.28 dB was achieved respectively and the response time was 24 s and 1 s, respectively. These results demonstrate that LuPc2 is a kind of NIR EC material and it has potential application for variable optical attenuator. (C) 2004 Elsevier B.V. All rights reserved. |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000226261900004 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/57495] |
专题 | 中国科学院化学研究所 |
通讯作者 | Zhang, DJ |
作者单位 | 1.Carleton Univ, Dept Chem, Ottawa, ON K1S 5B6, Canada 2.Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 3.Shandong Univ, Dept Chem, Jinan 250100, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, DJ,Lu, FL,Huang, HC,et al. Near infrared electrochromism of lutetium phthalocyanine[J]. SYNTHETIC METALS,2005,148(2):123-126. |
APA | Zhang, DJ.,Lu, FL.,Huang, HC.,Wang, J.,Yu, H.,...&Wang, ZY.(2005).Near infrared electrochromism of lutetium phthalocyanine.SYNTHETIC METALS,148(2),123-126. |
MLA | Zhang, DJ,et al."Near infrared electrochromism of lutetium phthalocyanine".SYNTHETIC METALS 148.2(2005):123-126. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论