Toughening poly(3-hydroxybutyrate) with propylene carbonate plasticized poly(propylene carbonate) | |
Zhou, Linyao1,2; Zhao, Guiyan1; Yin, Jinghua1; Jiang, Wei1 | |
刊名 | E-POLYMERS |
2014-07-01 | |
卷号 | 14期号:4 |
关键词 | Biodegradable Polymers Brittle-ductile Transition Impact Toughness Modulus Plasticizing |
ISSN号 | 1618-7229 |
DOI | 10.1515/epoly-2013-0069 |
英文摘要 | Poly(3-hydroxybutyrate) (PHB)/poly(propylene carbonate) (PPC) blends containing various amounts of plasticizer propylene carbonate (PC) were prepared, and the toughness of the blends as a function of temperature was studied. It was found that the brittle-ductile transition temperature (T-BD) of PHB toughened by PPC decreased from 60 degrees C to 10 degrees C with the increase in PC content. As PC is the plasticizer of PPC, the mechanical properties, such as Young's modulus of plasticized PPC with different PC contents, were also studied. Sequentially, the relationship between T BD and the ratio of the Young's modulus (E-1) of the PHB matrix to that of the plasticized PPC elastomer (E-2) was investigated. It was found that the Young's modulus of plasticized PPC should be considerably lower than that of the PHB matrix in order to obtain 'the tough PHB/plasticized PPC blends at a lower temperature. In contrast, the morphology of the dispersed particles also had an important influence on the toughness. When the plasticizer content was more than 20 wt.%, the PPC particles became more spherical and smaller. The toughness could be considerably improved accordingly. |
语种 | 英语 |
出版者 | WALTER DE GRUYTER GMBH |
WOS记录号 | WOS:000342083900006 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/51023] |
专题 | 中国科学院化学研究所 |
通讯作者 | Zhao, Guiyan |
作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Zhou, Linyao,Zhao, Guiyan,Yin, Jinghua,et al. Toughening poly(3-hydroxybutyrate) with propylene carbonate plasticized poly(propylene carbonate)[J]. E-POLYMERS,2014,14(4). |
APA | Zhou, Linyao,Zhao, Guiyan,Yin, Jinghua,&Jiang, Wei.(2014).Toughening poly(3-hydroxybutyrate) with propylene carbonate plasticized poly(propylene carbonate).E-POLYMERS,14(4). |
MLA | Zhou, Linyao,et al."Toughening poly(3-hydroxybutyrate) with propylene carbonate plasticized poly(propylene carbonate)".E-POLYMERS 14.4(2014). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论