High Energy Density and Discharging Efficiency Achieved in Chlorinated Polyethylene Films for High Energy-Storage Applications | |
Zhao, Yifei1; Li, Qian2; Zhang, Xiao3; Li, Huayi2; Lu, Junyong3; Zhang, Zhicheng1 | |
刊名 | MACROMOLECULAR CHEMISTRY AND PHYSICS
![]() |
2018-04-01 | |
卷号 | 219期号:8 |
关键词 | Chlorinated Polyethylene (Cpe) Energy Storage High Discharging Efficiency Capacitors |
ISSN号 | 1022-1352 |
DOI | 10.1002/macp.201700621 |
英文摘要 | Polymeric dielectric materials with high energy density (U-e), elevated breakdown strength (E-b), and high discharging efficiency (eta) are in demand for high-pulse metalized film capacitor application. In the present work, a randomly chlorinated polyethylene (CPE) with 71 wt% Cl moiety is fabricated in thin film (8-10 mu m). Thanks to the high Cl content, CPE exhibits a rather high glass transition temperature (approximate to 110 degrees C) and a Young's modulus of 2.6 GPa, which may address its high E-b. The random dispersion of Cl atoms onto the polymer chain is responsible for the well-maintained medium permittivity (3-4) and low loss at elevated temperature. Both factors result in the rather high U-e (about 12 J cm(-3)) and high eta (about 83%) under an electric field of 700 MV m(-1). Its higher energy-storage capability and operating temperature make CPE a promising polymeric dielectric for high-pulse metalized film capacitor applications. |
语种 | 英语 |
出版者 | WILEY-V C H VERLAG GMBH |
WOS记录号 | WOS:000430396100009 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/45941] ![]() |
专题 | 中国科学院化学研究所 |
通讯作者 | Li, Huayi; Zhang, Zhicheng |
作者单位 | 1.Xi An Jiao Tong Univ, Sch Sci, Dept Appl Chem, Xian 710049, Shaanxi, Peoples R China 2.Chinese Acad Sci, Inst Chem, Joint Lab Polymer Sci & Mat, Beijing 100190, Peoples R China 3.Naval Univ Engn, Natl Key Lab Sci & Technol Vessel Integrated Powe, Wuhan 430034, Hubei, Peoples R China |
推荐引用方式 GB/T 7714 | Zhao, Yifei,Li, Qian,Zhang, Xiao,et al. High Energy Density and Discharging Efficiency Achieved in Chlorinated Polyethylene Films for High Energy-Storage Applications[J]. MACROMOLECULAR CHEMISTRY AND PHYSICS,2018,219(8). |
APA | Zhao, Yifei,Li, Qian,Zhang, Xiao,Li, Huayi,Lu, Junyong,&Zhang, Zhicheng.(2018).High Energy Density and Discharging Efficiency Achieved in Chlorinated Polyethylene Films for High Energy-Storage Applications.MACROMOLECULAR CHEMISTRY AND PHYSICS,219(8). |
MLA | Zhao, Yifei,et al."High Energy Density and Discharging Efficiency Achieved in Chlorinated Polyethylene Films for High Energy-Storage Applications".MACROMOLECULAR CHEMISTRY AND PHYSICS 219.8(2018). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论