Influences of morphology and structure on Mn-based multi-step thermochemical H2O splitting cycle | |
Jiang, Zongxuan1; Chen, Zhenpan1,2; Jiang, Qingqing1; Tong, Jinhui1; Yang, Min1; Li, Can1 | |
刊名 | SOLAR ENERGY
![]() |
2016-05-01 | |
卷号 | 129页码:236-243 |
关键词 | Solar Energy Multi-step H2o Splitting Hydrogen Manganese Ferrite |
ISSN号 | 0038-092X |
DOI | 10.1016/j.solener.2015.12.051 |
文献子类 | Article |
英文摘要 | The multi-step thermochemical water splitting cycle based on MnFe2O4 Na2CO3 has emerged as an attractive process due to its relatively low reaction temperature. The main challenges are how to enhance its H-2/O-2 release rates and capacities. Herein, a series of MnFe2O4 with different microstructures synthesized by hydrothermal method were tested in H2O splitting reaction. It was found that MnFe2O4 samples with smaller particle size and fine crystallinity exhibited higher H-2 production which was benefit from enhanced intimate contact between homogeneous particles and better ionic transport within fine crystals. In order to enhance the reaction kinetics of the O-2 release reaction, a hydrolysis treatment was introduced to the multi-step cycle. As a result, the lamellar structure of Na+ extracted Na1-x(Mn1/3Fe2/3)O-2 oxide became unstable and collapsed into cubic MnFe2O4 spinel structure more easily under heating, a structure characteristic suitable for O-2 release reaction. Compared to direct O-2 release reaction between layered Na(Mn1/3Fe2/3)O-2 oxide and CO2, the hydrolysis treatment lead to much faster reaction rate. (C) 2016 Elsevier Ltd. All rights reserved. |
WOS关键词 | OXYGEN-RELEASING STEP ; HYDROGEN-PRODUCTION ; MNFE2O4-NA2CO3 SYSTEM ; MAGNETIC-PROPERTIES ; MANGANESE FERRITE ; KINETIC-ANALYSIS ; CO2 ; OXIDES ; DISSOCIATION ; ENHANCEMENT |
WOS研究方向 | Energy & Fuels |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:000373866800022 |
内容类型 | 期刊论文 |
源URL | [http://cas-ir.dicp.ac.cn/handle/321008/170724] ![]() |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
通讯作者 | Li, Can |
作者单位 | 1.Chinese Acad Sci, Dalian Natl Lab Clean Energy, Dalian Inst Chem Phys, State Key Lab Catalysis, 457 Zhongshan Rd, Dalian 116023, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Jiang, Zongxuan,Chen, Zhenpan,Jiang, Qingqing,et al. Influences of morphology and structure on Mn-based multi-step thermochemical H2O splitting cycle[J]. SOLAR ENERGY,2016,129:236-243. |
APA | Jiang, Zongxuan,Chen, Zhenpan,Jiang, Qingqing,Tong, Jinhui,Yang, Min,&Li, Can.(2016).Influences of morphology and structure on Mn-based multi-step thermochemical H2O splitting cycle.SOLAR ENERGY,129,236-243. |
MLA | Jiang, Zongxuan,et al."Influences of morphology and structure on Mn-based multi-step thermochemical H2O splitting cycle".SOLAR ENERGY 129(2016):236-243. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论