Growth of crack-free gan films on si(111) substrate by using al-rich aln buffer layer | |
Lu, Y; Cong, GW; Liu, XL; Lu, DC; Zhu, QS; Wang, XH; Wu, JJ; Wang, ZG | |
刊名 | Journal of applied physics |
2004-11-01 | |
卷号 | 96期号:9页码:4982-4988 |
ISSN号 | 0021-8979 |
DOI | 10.1063/1.1787588 |
通讯作者 | Lu, y(yuanlu@semi.ac.cn) |
英文摘要 | Gan epilayers were grown on si(111) substrate by metalorganic chemical vapor deposition. by using the al-rich aln buffer which contains al beyond stoichiometry, crack-free gan epilayers with 1 mum thickness were obtained. through x-ray diffraction (xrd) and secondary ion mass spectroscopy analyses, it was found that a lot of al atoms have diffused into the under part of the gan epilayer from the al-rich aln buffer, which results in the formation of an alxga1-xn layer at least with 300 nm thickness in the 1 mum thick gan epilayer. the al fraction x was estimated by xrd to be about 2.5%. x-ray photoelectron spectroscopy depth analysis was also applied to investigate the stoichiometry in the al-rich buffer before gan growth. it is suggested that the underlayer alxga1-xn originated from al diffusion probably provides a compressive stress to the upper part of the gan epilayer, which counterbalances a part of tensile stress in the gan epilayer during cooling down and consequently reduces the cracks of the film effectively. the method using the al diffusion effect to form a thick algan layer is really feasible to achieve the crack-free gan films and obtain a high crystal quality simultaneously. (c) 2004 american institute of physics. |
WOS关键词 | CHEMICAL-VAPOR-DEPOSITION ; LIGHT-EMITTING-DIODES ; INTERMEDIATE LAYER ; INTERLAYERS ; STRESS ; SAPPHIRE ; EPITAXY ; RATIO ; MOCVD |
WOS研究方向 | Physics |
WOS类目 | Physics, Applied |
语种 | 英语 |
出版者 | AMER INST PHYSICS |
WOS记录号 | WOS:000224799300040 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2426249 |
专题 | 半导体研究所 |
通讯作者 | Lu, Y |
作者单位 | Chinese Acad Sci, Inst Semicond, Key Lab Semicond Mat Sci, Beijing 100083, Peoples R China |
推荐引用方式 GB/T 7714 | Lu, Y,Cong, GW,Liu, XL,et al. Growth of crack-free gan films on si(111) substrate by using al-rich aln buffer layer[J]. Journal of applied physics,2004,96(9):4982-4988. |
APA | Lu, Y.,Cong, GW.,Liu, XL.,Lu, DC.,Zhu, QS.,...&Wang, ZG.(2004).Growth of crack-free gan films on si(111) substrate by using al-rich aln buffer layer.Journal of applied physics,96(9),4982-4988. |
MLA | Lu, Y,et al."Growth of crack-free gan films on si(111) substrate by using al-rich aln buffer layer".Journal of applied physics 96.9(2004):4982-4988. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论