Microstructure, mechanical, thermal, and oxidation properties of a zr-2[al(si)](4)c-5-sic composite prepared by in situ reaction/hot-pressing | |
He, Ling-Feng1,2; Li, Fang-Zhi1,2; Lu, Xin-Po1,2; Bao, Yi-Wang1; Zhou, Yan-Chun1 | |
刊名 | Journal of the european ceramic society
![]() |
2010-08-01 | |
卷号 | 30期号:11页码:2147-2154 |
关键词 | Carbides Microstructure Mechanical properties Thermal properties Corrosion |
ISSN号 | 0955-2219 |
DOI | 10.1016/j.jeurceramsoc.2010.02.005 |
通讯作者 | Zhou, yan-chun() |
英文摘要 | The microstructure, mechanical and thermal properties. as well as oxidation behavior, of in situ hot-pressed zr-2[al(si)](4)c-5-30 vol % sic composite have been characterized the microstructure is composed of elongated zr-2[al(si)](4)c-5 grains and embedded sic particles the composite shows superior hardness (vickers hardness of 16 4 gpa), stiffness (young's modulus of 386 gpa), strength (bending strength of 353 mpa), and toughness (fracture toughness of 6.62 mpa m(1/2)) compared to a monolithic zr-2[al(si)](4)c-5 ceramic stiffness is maintained up to 1600 degrees c (323 gpa) due to clean grain boundaries with no glassy phase the composite also exhibits higher specific heat capacity and thermal conductivity as well as better oxidation resistance compared to zr-2[al(si)](4)c-5 (c) 2010 elsevier ltd. all rights reserved |
WOS关键词 | HIGH-TEMPERATURE ; TI3SI(AL)C-2/SIC COMPOSITES ; FRACTURE-TOUGHNESS ; INTERNAL-FRICTION ; SILICON-CARBIDE ; C CERAMICS ; ZR2AL3C4 ; ADDITIVES ; STRENGTH ; ALUMINUM |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Ceramics |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000279569900002 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2410006 |
专题 | 中国科学院大学 |
通讯作者 | Zhou, Yan-Chun |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | He, Ling-Feng,Li, Fang-Zhi,Lu, Xin-Po,et al. Microstructure, mechanical, thermal, and oxidation properties of a zr-2[al(si)](4)c-5-sic composite prepared by in situ reaction/hot-pressing[J]. Journal of the european ceramic society,2010,30(11):2147-2154. |
APA | He, Ling-Feng,Li, Fang-Zhi,Lu, Xin-Po,Bao, Yi-Wang,&Zhou, Yan-Chun.(2010).Microstructure, mechanical, thermal, and oxidation properties of a zr-2[al(si)](4)c-5-sic composite prepared by in situ reaction/hot-pressing.Journal of the european ceramic society,30(11),2147-2154. |
MLA | He, Ling-Feng,et al."Microstructure, mechanical, thermal, and oxidation properties of a zr-2[al(si)](4)c-5-sic composite prepared by in situ reaction/hot-pressing".Journal of the european ceramic society 30.11(2010):2147-2154. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论