Pressureless sintering of machinable al2o3/lapo4 composites in n-2 atmosphere | |
Gong, GL; Zhang, BL; Zhang, HR; Li, WL | |
刊名 | Ceramics international |
2006 | |
卷号 | 32期号:3页码:349-352 |
关键词 | Al2o3/lapo4 composite Pressureless sintering Machinable |
ISSN号 | 0272-8842 |
DOI | 10.1016/j.ceramint.2005.03.002 |
通讯作者 | Gong, gl(glgong@mail.sic.ac.cn) |
英文摘要 | Al2o3/lapo4 composites were fabricated by pressureless sintering in n-2 atmosphere. the effect of sintering ternperature and sintering time on densification was examined, as well as the dependence of mechanical properties and microstructure on lapo4 content. provided the ratio of la/p was close to 1:1, no reactions were observed after 2 h at 1650 degrees c in n-2 atmosphere. the 30 wt.% lapo4/al2o3 composites could be machined using cemented carbide drills as those pressureless sintered in air. laal11o18 was formed when the composite was sintered at 1700 degrees c for 1 h in n-2 atmosphere, and the composites were not machinable. (c) 2005 elsevier ltd and techna group s.r.l. all rights reserved. |
WOS关键词 | CERAMIC COMPOSITES ; HIGH-STRENGTH ; MICROSTRUCTURE ; STABILITY |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Ceramics |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000235857900020 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2378735 |
专题 | 中国科学院大学 |
通讯作者 | Gong, GL |
作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Gong, GL,Zhang, BL,Zhang, HR,et al. Pressureless sintering of machinable al2o3/lapo4 composites in n-2 atmosphere[J]. Ceramics international,2006,32(3):349-352. |
APA | Gong, GL,Zhang, BL,Zhang, HR,&Li, WL.(2006).Pressureless sintering of machinable al2o3/lapo4 composites in n-2 atmosphere.Ceramics international,32(3),349-352. |
MLA | Gong, GL,et al."Pressureless sintering of machinable al2o3/lapo4 composites in n-2 atmosphere".Ceramics international 32.3(2006):349-352. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论