Pt4ZrO2/C cathode catalyst for improved durability in high temperature PEMFC based on H3PO4 doped PBI | |
Liu, Gang; Zhang, Huamin; Zhai, Yunfeng; Zhang, Yu; Xu, Dongyan; Shao, Zhi-gang | |
刊名 | electrochemistry communications |
2007 | |
卷号 | 9期号:1页码:135-141 |
关键词 | Pt4ZrO2/C oxygen reduction durability potential sweep test high temperature PEMFC |
通讯作者 | 张华民 |
产权排序 | 1;1 |
英文摘要 | in this paper, pt4zro2/c was prepared and compared with commercial pt/c (46.6 wt.% tkk) in terms of the durability as cathode catalyst in a high temperature proton exchange membrane fuel cell (pemfc) based on h3po4 doped polybenzimidazole (pbi) by a potential sweep test. the catalysts before and after the potential sweep test were characterized by rotating disk electrode (rde), xray diffraction (xrd), transmission electron microscopy (tem) and inductively coupled plasma-atomic emission spectroscopy (icp-aes). after 3000 cycles potential sweep test, the overall performance loss of the pt4zro2/c membrane electrode assembly (mea) was less than that of the pt/c mea. the ride results demonstrated that the oxygen reduction reaction (orr) activity of the as-prepared pt4zro2/c is nearly the same as tkk-pt/c. the xrd and tem results showed that pt4zro2/c catalyst presented higher sintering resistance than commercial pt/c catalyst during the potential sweep test. this may be attributed to the addition of zro2, which acts an anchor to inhibit the adjacent platinum particles to agglomerate. the icp-aes results of pt4zro2/c cathode catalyst before and after the potential sweep test showed that the composition of pt and zr were very near the nominal atomic ratio of pt:zr, which reflected that pt4zro2/c catalyst had a good stability during the potential sweep test. in brief, the preliminary results indicate that pt4zro2/c catalyst is a good candidate of pt/c catalyst in high temperature pemfc based on h3po4 doped pbi for achieving longer cell life-time and higher cell performance. (c) 2006 elsevier b.v. all rights reserved. |
WOS标题词 | science & technology ; physical sciences |
类目[WOS] | electrochemistry |
研究领域[WOS] | electrochemistry |
关键词[WOS] | supported platinum catalysts ; membrane fuel-cells ; surface-area loss ; oxygen reduction ; polymer electrolyte ; phosphoric-acid ; carbon ; alloys ; electrocatalysis |
收录类别 | SCI |
原文出处 | true |
语种 | 英语 |
WOS记录号 | WOS:000243847600025 |
公开日期 | 2010-11-30 |
内容类型 | 期刊论文 |
源URL | [http://159.226.238.44/handle/321008/98987] |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Lab PEMFC Key Mat & Technol, Dalian 116023, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Liu, Gang,Zhang, Huamin,Zhai, Yunfeng,et al. Pt4ZrO2/C cathode catalyst for improved durability in high temperature PEMFC based on H3PO4 doped PBI[J]. electrochemistry communications,2007,9(1):135-141. |
APA | Liu, Gang,Zhang, Huamin,Zhai, Yunfeng,Zhang, Yu,Xu, Dongyan,&Shao, Zhi-gang.(2007).Pt4ZrO2/C cathode catalyst for improved durability in high temperature PEMFC based on H3PO4 doped PBI.electrochemistry communications,9(1),135-141. |
MLA | Liu, Gang,et al."Pt4ZrO2/C cathode catalyst for improved durability in high temperature PEMFC based on H3PO4 doped PBI".electrochemistry communications 9.1(2007):135-141. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论