Solidification structure of C2.08Cr25.43Si1.19Mn0.43Fe70.87 powders fabricated by high pressure gas atomization | |
Dai, Yongxiang[1]; Yang, Min[2]; Song, Changjiang[3]; Han, Qingyou[4]; Zhai, Qijie[5] | |
刊名 | MATERIALS CHARACTERIZATION |
2010 | |
卷号 | 61页码:116-122 |
关键词 | Atomization High chromium white cast iron Cooling rate Microstructure |
ISSN号 | 1044-5803 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2318274 |
专题 | 上海大学 |
作者单位 | 1.Shanghai Key Laboratory of Modern Metallurgy and Materials Processing, Shanghai University, Shanghai, China 2.Mechanical Engineering Technology Department, Purdue University, United States |
推荐引用方式 GB/T 7714 | Dai, Yongxiang[1],Yang, Min[2],Song, Changjiang[3],et al. Solidification structure of C2.08Cr25.43Si1.19Mn0.43Fe70.87 powders fabricated by high pressure gas atomization[J]. MATERIALS CHARACTERIZATION,2010,61:116-122. |
APA | Dai, Yongxiang[1],Yang, Min[2],Song, Changjiang[3],Han, Qingyou[4],&Zhai, Qijie[5].(2010).Solidification structure of C2.08Cr25.43Si1.19Mn0.43Fe70.87 powders fabricated by high pressure gas atomization.MATERIALS CHARACTERIZATION,61,116-122. |
MLA | Dai, Yongxiang[1],et al."Solidification structure of C2.08Cr25.43Si1.19Mn0.43Fe70.87 powders fabricated by high pressure gas atomization".MATERIALS CHARACTERIZATION 61(2010):116-122. |