High relative density tin bronze parts directly manufactured by selective laser melting (EI收录)
Bai, Yu-Chao[1]; Yang, Yong-Qiang[1]; Wang, Di[1]; Wang, An-Min[1]
刊名Guangxue Jingmi Gongcheng/Optics and Precision Engineering
2016
卷号24页码:484-492
关键词3D printers Computerized tomography Genetic algorithms Melting Neural networks Optimization Parameter estimation Scanning Stereo image processing Surface defects Surface topography Thin walled structures Tin Tin alloys Wind turbines
URL标识查看原文
内容类型期刊论文
URI标识http://www.corc.org.cn/handle/1471x/2196513
专题华南理工大学
作者单位1.[1] College of Mechanical and Automobile Engineering, South China University of Technology, Guangzhou
2.Guangdong
3.510640, China
推荐引用方式
GB/T 7714
Bai, Yu-Chao[1],Yang, Yong-Qiang[1],Wang, Di[1],等. High relative density tin bronze parts directly manufactured by selective laser melting (EI收录)[J]. Guangxue Jingmi Gongcheng/Optics and Precision Engineering,2016,24:484-492.
APA Bai, Yu-Chao[1],Yang, Yong-Qiang[1],Wang, Di[1],&Wang, An-Min[1].(2016).High relative density tin bronze parts directly manufactured by selective laser melting (EI收录).Guangxue Jingmi Gongcheng/Optics and Precision Engineering,24,484-492.
MLA Bai, Yu-Chao[1],et al."High relative density tin bronze parts directly manufactured by selective laser melting (EI收录)".Guangxue Jingmi Gongcheng/Optics and Precision Engineering 24(2016):484-492.
个性服务
查看访问统计
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。


©版权所有 ©2017 CSpace - Powered by CSpace