Reduced Fracture Toughness of Metallic Glass at Cryogenic Temperature | |
Zhou, Yihao[1]; Liu, Jiaxin[2]; Han, Dongxue[3]; Chen, Xiangru[4]; Wang, Gang[5]; Zhai, Qijie[6] | |
刊名 | METALS |
2017 | |
卷号 | 7 |
关键词 | metallic glass fracture toughness cryogenic temperature fractographic evolution |
ISSN号 | 2075-4701 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2188426 |
专题 | 上海大学 |
作者单位 | 1.[1]Shanghai Univ, Inst Mat, Lab Microstruct, Shanghai 20044, Peoples R China. 2.Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 3.[2]Shanghai Univ, Inst Mat, Lab Microstruct, Shanghai 20044, Peoples R China. 4.Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 5.[3]Shanghai Univ, Inst Mat, Lab Microstruct, Shanghai 20044, Peoples R China. 6.Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 7.[4]Shanghai Univ, Inst Mat, Lab Microstruct, Shanghai 20044, Peoples R China. 8.Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. 9.[5]Shanghai Univ, Inst Mat, Lab Microstruct, Shanghai 20044, Peoples R China. 10.Shanghai Univ, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China.,Shanghai Univ, Shanghai Key Lab Adv Ferromet, Shanghai 200072, Peoples R China.,Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China. |
推荐引用方式 GB/T 7714 | Zhou, Yihao[1],Liu, Jiaxin[2],Han, Dongxue[3],et al. Reduced Fracture Toughness of Metallic Glass at Cryogenic Temperature[J]. METALS,2017,7. |
APA | Zhou, Yihao[1],Liu, Jiaxin[2],Han, Dongxue[3],Chen, Xiangru[4],Wang, Gang[5],&Zhai, Qijie[6].(2017).Reduced Fracture Toughness of Metallic Glass at Cryogenic Temperature.METALS,7. |
MLA | Zhou, Yihao[1],et al."Reduced Fracture Toughness of Metallic Glass at Cryogenic Temperature".METALS 7(2017). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论