Fatigue Fracture Characteristics of Ti6Al4V Subjected to Ultrasonic Nanocrystal Surface Modification | |
Xiaojian Cao; Luopeng Xu; Xiaoli Xu; Qingyuan Wang | |
刊名 | Metals
![]() |
2018 | |
卷号 | Vol.8 No.1页码:77 |
关键词 | nanocrystal surface modification UNSM Ti6Al4V fatigue crack |
ISSN号 | 2075-4701 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/1908824 |
专题 | 四川大学 |
作者单位 | School of Architecture Engineering, Nantong University, Nantong 226019, China Department of Mechanics and Engineering Science, Sichuan University, Chengdu 610065, China School of Architecture Engineering, Nantong University, Nantong 226019, China School of Aeronautics and Astronautics, Sichuan University, Chengdu 610065, China |
推荐引用方式 GB/T 7714 | Xiaojian Cao,Luopeng Xu,Xiaoli Xu,et al. Fatigue Fracture Characteristics of Ti6Al4V Subjected to Ultrasonic Nanocrystal Surface Modification[J]. Metals,2018,Vol.8 No.1:77. |
APA | Xiaojian Cao,Luopeng Xu,Xiaoli Xu,&Qingyuan Wang.(2018).Fatigue Fracture Characteristics of Ti6Al4V Subjected to Ultrasonic Nanocrystal Surface Modification.Metals,Vol.8 No.1,77. |
MLA | Xiaojian Cao,et al."Fatigue Fracture Characteristics of Ti6Al4V Subjected to Ultrasonic Nanocrystal Surface Modification".Metals Vol.8 No.1(2018):77. |