Flexural fracture mechanisms and fatigue behaviors of BiTiO-based high-temperature piezoceramics sintered at different temperatures | |
Shaoxiong Xie; Jiageng Xu; Yu Chen; Zhi Tan; Rui Nie; Qingyuan Wang; Jianguo Zhu | |
刊名 | Ceramics International
![]() |
2018 | |
关键词 | Bi4Ti3O12 ceramics Microstructures Fracture mechanisms Fatigue behaviors |
ISSN号 | 0272-8842 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/1870365 |
专题 | 四川大学 |
作者单位 | 1.College of Materials Science and Engineering, Sichuan University, Chengdu 610065, China 2.School of Architecture and Civil Engineering, Chengdu University, Chengdu 610106, China 3.a College of Architecture and Environment, Sichuan University, Chengdu 610065, China |
推荐引用方式 GB/T 7714 | Shaoxiong Xie,Jiageng Xu,Yu Chen,et al. Flexural fracture mechanisms and fatigue behaviors of BiTiO-based high-temperature piezoceramics sintered at different temperatures[J]. Ceramics International,2018. |
APA | Shaoxiong Xie.,Jiageng Xu.,Yu Chen.,Zhi Tan.,Rui Nie.,...&Jianguo Zhu.(2018).Flexural fracture mechanisms and fatigue behaviors of BiTiO-based high-temperature piezoceramics sintered at different temperatures.Ceramics International. |
MLA | Shaoxiong Xie,et al."Flexural fracture mechanisms and fatigue behaviors of BiTiO-based high-temperature piezoceramics sintered at different temperatures".Ceramics International (2018). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论