Corrosion Behavior of SiCf/SiC Composites in High Temperature Fluoride Salt Environment | |
Wang, Hong-Da1,2,3; Zhou, Hai-Jun1,2; Dong, Shao-Ming1,2; Wang, Zhen1,2; Hu, Jian-Bao1,2; Feng, Qian4 | |
刊名 | Wuji Cailiao Xuebao/Journal of Inorganic Materials
![]() |
2017 | |
卷号 | 32期号:11页码:1133-1140 |
ISSN号 | 1000324X |
DOI | 10.15541/jim20170010 |
英文摘要 | Corrosion behavior of SiCf/SiC composites, which were prepared via molten infiltration(MI), polymer impregnation and pyrolysis(PIP), and chemical vapor infiltration process(CVI), respectively, was studied by immersion in 46.5mol% LiF-11.5mol% NaF-42.0mol% KF eutectic salt at 800. The evolution of phase composition and microstructure was characterized by X-ray diffraction and scanning electron microscope with energy dispersive spectrometer. The SiC matrix of SiCf/SiC composites, derived from different preparation process, has different compositions and microstructures, leading to various compatibility with fluoride salt at high temperature. Residual free Si in MI-SiC matrix and O-contained phase in PIP-SiC matrix are the weak area with worse corrosion resistance in liquid fluoride salt and will be corroded preferentially in terms of thermodynamic. Due to the higher purity and better crystallinity over the MI-SiC matrix and PIP-SiC matrix, CVI-SiC matrix shows more excellent compatibility with fluoride salt at high temperature and has the smallest corrosion rate of 0.0445 μg/(mm2·h). Least weak area confined to the O-rich boundaries between deposited layers may account for the good corrosion resistance of CVI SiC matrix. © 2017, Science Press. All right reserved. |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/25703] ![]() |
专题 | 中国科学院上海硅酸盐研究所 |
作者单位 | 1.Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics Chinese Academy of Sciences, Shanghai; 200050, China; 2.State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics Chinese Academy of Sciences, Shanghai; 200050, China; 3.School of Graduate, University of Chinese Academy of Sciences, Beijing; 100049, China; 4.Analysis and Testing Center, Donghua University, Shanghai; 201600, China |
推荐引用方式 GB/T 7714 | Wang, Hong-Da,Zhou, Hai-Jun,Dong, Shao-Ming,et al. Corrosion Behavior of SiCf/SiC Composites in High Temperature Fluoride Salt Environment[J]. Wuji Cailiao Xuebao/Journal of Inorganic Materials,2017,32(11):1133-1140. |
APA | Wang, Hong-Da,Zhou, Hai-Jun,Dong, Shao-Ming,Wang, Zhen,Hu, Jian-Bao,&Feng, Qian.(2017).Corrosion Behavior of SiCf/SiC Composites in High Temperature Fluoride Salt Environment.Wuji Cailiao Xuebao/Journal of Inorganic Materials,32(11),1133-1140. |
MLA | Wang, Hong-Da,et al."Corrosion Behavior of SiCf/SiC Composites in High Temperature Fluoride Salt Environment".Wuji Cailiao Xuebao/Journal of Inorganic Materials 32.11(2017):1133-1140. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论