Temperature induced high charge–discharge performances in lead-free Bi0.5Na0.5TiO3-based ergodic relaxor ferroelectric ceramics | |
Li, Feng1,2,3; Yang, Ke1; Liu, Xing1; Zou, Jian2,3; Zhai, Jiwei1; Shen, Bo1; Li, Peng1; Shen, Jie1; Liu, Baihui1; Chen, Pan1 | |
刊名 | Scripta Materialia |
2017 | |
卷号 | 141页码:15-19 |
ISSN号 | 13596462 |
DOI | 10.1016/j.scriptamat.2017.07.010 |
英文摘要 | The temperature dependence of energy storage and charge–discharge properties of a lead–free 0.62Bi0.5Na0.5TiO3–0.06BaTiO3–0.32(Sr0.7Bi0.20.1)TiO3ergodic relaxor ferroelectric ceramic were investigated. The energy storage density was maintained ≥ 0.5 J/cm3up to 140 °C with a high efficiency ≥ 90%. The stored energy was released in sub–microsecond durations and charge–discharge performances were enhanced as temperature increased to 160 °C. This ceramic possessed an enhanced power density 18.2 MW/cm3and large current density 606 A/cm2. All results showed that this ergodic relaxor ferroelectric ceramics appeared very promising for pulse capacitor applications. © 2017 Acta Materialia Inc. |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/25765] |
专题 | 中国科学院上海硅酸盐研究所 |
作者单位 | 1.Key Laboratory of Advanced Civil Engineering Materials of Ministry of Education, School of Materials Science & Engineering, Tongji University, 4800 Caoan road, Shanghai; 201804, China; 2.Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 3.University of Chinese Academy of Sciences, Beijing; 100049, China |
推荐引用方式 GB/T 7714 | Li, Feng,Yang, Ke,Liu, Xing,et al. Temperature induced high charge–discharge performances in lead-free Bi0.5Na0.5TiO3-based ergodic relaxor ferroelectric ceramics[J]. Scripta Materialia,2017,141:15-19. |
APA | Li, Feng.,Yang, Ke.,Liu, Xing.,Zou, Jian.,Zhai, Jiwei.,...&Zeng, Huarong.(2017).Temperature induced high charge–discharge performances in lead-free Bi0.5Na0.5TiO3-based ergodic relaxor ferroelectric ceramics.Scripta Materialia,141,15-19. |
MLA | Li, Feng,et al."Temperature induced high charge–discharge performances in lead-free Bi0.5Na0.5TiO3-based ergodic relaxor ferroelectric ceramics".Scripta Materialia 141(2017):15-19. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论