Fabrication and microwave dielectric properties of CuO-B2O3-Li2O glass-ceramic with ultra-low sintering temperature

doi:10.1016/j.ceramint.2017.05.190

	Fabrication and microwave dielectric properties of CuO-B2O3-Li2O glass-ceramic with ultra-low sintering temperature
	Ma, Mingsheng 1; Fu, Zhengqian 2,3; Liu, Zhifu 1; Li, Yongxiang 1,3,4
刊名	Ceramics International
	2017
卷号	43 页码:S292-S295
ISSN号	02728842
DOI	10.1016/j.ceramint.2017.05.190
英文摘要	CuO-B2O3-Li2O (CBL) glass-ceramic with a composition of 32 wt% CuO − 63 wt% B2O3− 5 wt% Li2O was prepared through conventional glass-ceramic route. The CBL glass-ceramic could be densified well by sintering at 625 °C for 30 min. The X-Ray diffraction (XRD) and transmission electron microscopy (TEM) analysis indicated that the CuB2O4phase was dominated in the sintered glass-ceramic, which showed excellent microwave dielectric properties with Εr= 5.84, Q×f = 10120 GHz (at 13.44 GHz), and τf= −33 ppm/°C. Furthermore, the CBL material is chemically compatible with both silver (Ag) and aluminum (Al) electrodes at their sintering temperatures. These properties indicate that the CBL glass-ceramic might be a promising ultra-low temperature co-fired ceramic (ULTCC) material for packaging substrate applications. © 2017 Elsevier Ltd and Techna Group S.r.l.
内容类型	期刊论文
源URL	[http://ir.sic.ac.cn/handle/331005/25859]
专题	中国科学院上海硅酸盐研究所
作者单位	1.The Key Lab of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 2.Analysis and Testing Center for Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 3.School of Physical Science and Technology, ShanghaiTech University, Shanghai; 201210, China; 4.School of Engineering, RMIT University, Melbourne; VIC; 3000, Australia
推荐引用方式 GB/T 7714	Ma, Mingsheng,Fu, Zhengqian,Liu, Zhifu,et al. Fabrication and microwave dielectric properties of CuO-B2O3-Li2O glass-ceramic with ultra-low sintering temperature[J]. Ceramics International,2017,43:S292-S295.
APA	Ma, Mingsheng,Fu, Zhengqian,Liu, Zhifu,&Li, Yongxiang.(2017).Fabrication and microwave dielectric properties of CuO-B2O3-Li2O glass-ceramic with ultra-low sintering temperature.Ceramics International,43,S292-S295.
MLA	Ma, Mingsheng,et al."Fabrication and microwave dielectric properties of CuO-B2O3-Li2O glass-ceramic with ultra-low sintering temperature".Ceramics International 43(2017):S292-S295.