Chemical process and solid solution formation in reactive hot pressed ZrB2–SiC ceramics doped with W | |
Liu, H.-L.1,2; Ma, H.-B.1,2; Liu, J.-X.1; Liu, H.-T.1; Zhang, G.-J.1 | |
刊名 | Advances in Applied Ceramics
![]() |
2017 | |
卷号 | 116期号:2页码:118-122 |
ISSN号 | 17436753 |
DOI | 10.1080/17436753.2016.1257256 |
英文摘要 | ZrB2–SiC doped with W was prepared from a mixture of Zr, Si, B4C and W via reactive hot pressing. The fully dense ZrB2–SiC–WB–ZrC ceramic was obtained at 1900°C for 60 min under 30 MPa in an argon atmosphere. Reaction path and solid solution characteristics of the starting powders were studied through a series of pressureless heat treatment at temperatures between 700 and 1500°C. The solid solution phases of (Zr, W)B2, (W, Zr)B and (Zr, W)C were formed directly by reactions between the precursors. Homogeneous distribution of solute atoms in solution and the solid solubilities were also studied. © 2016 Institute of Materials, Minerals and Mining. |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/25944] ![]() |
专题 | 中国科学院上海硅酸盐研究所 |
作者单位 | 1.State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Shanghai, China; 2.University of the Chinese Academy of Sciences, Beijing, China |
推荐引用方式 GB/T 7714 | Liu, H.-L.,Ma, H.-B.,Liu, J.-X.,et al. Chemical process and solid solution formation in reactive hot pressed ZrB2–SiC ceramics doped with W[J]. Advances in Applied Ceramics,2017,116(2):118-122. |
APA | Liu, H.-L.,Ma, H.-B.,Liu, J.-X.,Liu, H.-T.,&Zhang, G.-J..(2017).Chemical process and solid solution formation in reactive hot pressed ZrB2–SiC ceramics doped with W.Advances in Applied Ceramics,116(2),118-122. |
MLA | Liu, H.-L.,et al."Chemical process and solid solution formation in reactive hot pressed ZrB2–SiC ceramics doped with W".Advances in Applied Ceramics 116.2(2017):118-122. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论