Low Temperature Electrochemical Deposition of Aluminum in Organic Bases/Thiourea-Based Deep Eutectic Solvents | |
Wang, Jinfang1; Wang, Peng2; Wang, Qian3; Mou, Hongyu1; Cao, Bobo4; Yu, Dongkun1; Wang, Debao2; Zhang, Suojiang3; Mu, Tiancheng1 | |
刊名 | ACS SUSTAINABLE CHEMISTRY & ENGINEERING
![]() |
2018-11-05 | |
卷号 | 6期号:11页码:15480-15486 |
关键词 | Des Gamma-al2o3 Dispersion Low Temperature Electrodeposition Of Aluminum |
ISSN号 | 2168-0485 |
DOI | 10.1021/acssuschemeng.8b03942 |
英文摘要 | In this study, a series of novel quasi-deep eutectic solvents (QDESs) based on organic base and thiourea (TU) and its derivatives were formed. Among them, DBU/TU or methylthiourea (MTU) could be used for the formation of the stable gamma-Al2O3 colloid at quite a high concentration (0.6 mol %), which was verified by small-angle X-ray scattering (SAXS) experiments. The solution is highly fluidic with a viscosity of 46.2 mPa.s at 50 degrees C. The attenuated total reflection infrared spectra (ATR-IR), Al-27 nuclear magnetic resonance (NMR), and density functional theory (DFT) calculation proved that gamma-Al2O3 was coordinated with the sulfur atom of methylthiourea. Electrodepositing of aluminum from the system at a low temperature (50 degrees C) and atmospheric environment was achieved. The cyclic voltammogram indicated a good aluminum deposition peak at -0.26 V at 50 degrees C. SEM, EDS, and XRD pattern showed that homogeneous, pure, and adherent aluminum layers were obtained. Moreover, these DESs are versatile and can be used for dissolving other metals, metal sulfides, and metal oxides, including CoO, NiO, Ni2O3, MoO3, CuS, Fe, W, Cu, and V2VI3 chalcogenides. Therefore, this work extended the scope of green solvent and made an improvement in both low temperature electrolytic alumina and solution processing of other metal-based materials. |
资助项目 | National Natural Science Foundation of China[21773307] ; National Natural Science Foundation of China[21473252] ; Shandong Key Laboratory of Biochemical Analysis, Qingdao University of Science and Technology[QUSTHX201809] |
WOS关键词 | Ionic Liquids ; Inorganic Salts ; Electrodeposition ; Dissolution ; Complexes ; Urea ; Nanocrystalline ; Speciation ; Molecules ; Cellulose |
WOS研究方向 | Chemistry ; Science & Technology - Other Topics ; Engineering |
语种 | 英语 |
出版者 | AMER CHEMICAL SOC |
WOS记录号 | WOS:000449577200205 |
资助机构 | National Natural Science Foundation of China ; Shandong Key Laboratory of Biochemical Analysis, Qingdao University of Science and Technology |
内容类型 | 期刊论文 |
源URL | [http://ir.ipe.ac.cn/handle/122111/26661] ![]() |
专题 | 中国科学院过程工程研究所 |
通讯作者 | Mu, Tiancheng |
作者单位 | 1.Renmin Univ China, Dept Chem, 59 Zhongguancun St, Beijing 100872, Peoples R China 2.Qingdao Univ Sci & Technol, Coll Chem & Mol Engn, Shandong Key Lab Biochem Anal, Qingdao 266042, Peoples R China 3.Chinese Acad Sci, Inst Proc Engn, Beijing Key Lab Ion Liquids Clean Proc, Beijing 100190, Peoples R China 4.Tsinghua Univ, Dept Chem, MOE Key Lab Bioorgan Phosphorous Chem & Chem Biol, Beijing 100084, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Jinfang,Wang, Peng,Wang, Qian,et al. Low Temperature Electrochemical Deposition of Aluminum in Organic Bases/Thiourea-Based Deep Eutectic Solvents[J]. ACS SUSTAINABLE CHEMISTRY & ENGINEERING,2018,6(11):15480-15486. |
APA | Wang, Jinfang.,Wang, Peng.,Wang, Qian.,Mou, Hongyu.,Cao, Bobo.,...&Mu, Tiancheng.(2018).Low Temperature Electrochemical Deposition of Aluminum in Organic Bases/Thiourea-Based Deep Eutectic Solvents.ACS SUSTAINABLE CHEMISTRY & ENGINEERING,6(11),15480-15486. |
MLA | Wang, Jinfang,et al."Low Temperature Electrochemical Deposition of Aluminum in Organic Bases/Thiourea-Based Deep Eutectic Solvents".ACS SUSTAINABLE CHEMISTRY & ENGINEERING 6.11(2018):15480-15486. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论