Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment

doi:10.1016/j.jeurceramsoc.2017.04.028

	Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment
	Jiang, Nan 1,2; Liu, Qiang 2; Xie, Tengfei 1; Ma, Peng 1; Kou, Huamin 1; Pan, Yubai 3; Li, Jiang 1
刊名	Journal of the European Ceramic Society
	2017
卷号	37 期号:13 页码:4213-4216
ISSN号	09552219
DOI	10.1016/j.jeurceramsoc.2017.04.028
英文摘要	Highly transparent aluminum oxynitride (AlON) ceramics were fabricated by pressureless sintering with hot isostatic pressing (HIP) post-treatment. The experimental results showed that the optical transparency of AlON ceramics was improved markedly over the visible and near-infrared range by HIP at 1825 °C for 3 h in 200 MPa argon gas, which derived from the elimination of residual pores in the prepared ceramics. For AlON ceramics pre-sintered at 1800 °C, the transmittances of the sample increased from 63.6% to 84.8% at 600 nm and from 75.4% to 86.1% at 2000 nm, respectively. The average grain size of the HIPed sample was about 47.9 μm. © 2017 Elsevier Ltd
内容类型	期刊论文
源URL	[http://ir.sic.ac.cn/handle/331005/25499]
专题	中国科学院上海硅酸盐研究所
作者单位	1.Key Laboratory of Transparent Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 2.School of Materials Science and Engineering, Jiangsu University, Zhenjiang; Jiangsu; 212013, China; 3.Shanghai Normal University, Shanghai; 200234, China
推荐引用方式 GB/T 7714	Jiang, Nan,Liu, Qiang,Xie, Tengfei,et al. Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment[J]. Journal of the European Ceramic Society,2017,37(13):4213-4216.
APA	Jiang, Nan.,Liu, Qiang.,Xie, Tengfei.,Ma, Peng.,Kou, Huamin.,...&Li, Jiang.(2017).Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment.Journal of the European Ceramic Society,37(13),4213-4216.
MLA	Jiang, Nan,et al."Fabrication of highly transparent AlON ceramics by hot isostatic pressing post-treatment".Journal of the European Ceramic Society 37.13(2017):4213-4216.