Pore filling behavior of YSZ under CMAS attack: Implications for designing corrosion-resistant thermal barrier coatings | |
Shan, Xiao1; Luo, Lirong1; Chen, Wenfu1; Zou, Zhonghua1; Guo, Fangwei1; He, Limin2; Zhang, Aiping3; Zhao, Xiaofeng1; Xiao, Ping1,4 | |
刊名 | Journal of the American Ceramic Society |
2018 | |
卷号 | 101期号:12页码:5756-5770 |
ISSN号 | 00027820 |
DOI | 10.1111/jace.15790 |
英文摘要 | To understand the pore filling behavior in thermal barrier coatings during calcium-magnesium-alumino-silicate (CMAS) infiltration process, porous yttria-stabilized zirconia pellets with different sizes of spherical pores were prepared to simulate thermal barrier coatings. The pores (D50 ranging from 6 to 77 μm) were introduced to the pellets using poly methyl methacrylate as pore forming agents. Then the pellets were sintered to remove the pore forming agents and to achieve a similar volume fraction of porosity with thermal barrier coatings. After CMAS infiltration, only some small pores in the CMAS-infiltrated zones were filled by CMAS, whereas all large pores (larger than 13 μm) remained unfilled; besides, the results also show that even open pores can resist filling by CMAS. The reason may relate to pore diameters; if the diameter of a pore is relatively large, the pore surface will not be completely wetted by liquid CMAS, the liquid meniscus will be discontinuous, and therefore the pore cannot be filled. The key insight gained from this study is that introducing “CMAS-proof” pores into thermal barrier coatings may be a potential way to mitigate CMAS damage. © 2018 The American Ceramic Society |
出版者 | Blackwell Publishing Inc. |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/25176] |
专题 | 中国科学院上海硅酸盐研究所 |
作者单位 | 1.Shanghai Key Laboratory of Advanced High-temperature Materials and Precision Forming, Shanghai Jiao Tong University, Shanghai, China; 2.Beijing Institute of Aeronautical Materials, Beijing, China; 3.Konca Solar Cells Co., Ltd, Wuxi, China; 4.School of Materials, University of Manchester, Oxford Road, Manchester, United Kingdom |
推荐引用方式 GB/T 7714 | Shan, Xiao,Luo, Lirong,Chen, Wenfu,et al. Pore filling behavior of YSZ under CMAS attack: Implications for designing corrosion-resistant thermal barrier coatings[J]. Journal of the American Ceramic Society,2018,101(12):5756-5770. |
APA | Shan, Xiao.,Luo, Lirong.,Chen, Wenfu.,Zou, Zhonghua.,Guo, Fangwei.,...&Xiao, Ping.(2018).Pore filling behavior of YSZ under CMAS attack: Implications for designing corrosion-resistant thermal barrier coatings.Journal of the American Ceramic Society,101(12),5756-5770. |
MLA | Shan, Xiao,et al."Pore filling behavior of YSZ under CMAS attack: Implications for designing corrosion-resistant thermal barrier coatings".Journal of the American Ceramic Society 101.12(2018):5756-5770. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论