	Sol-gel derived Al-doped zinc oxide - Reduced graphene oxide nanocomposite thin films
	Lu, Huanming; Yu, Xiayang; Xu, Jian; Fang, Gang
刊名	JOURNAL OF ALLOYS AND COMPOUNDS
	2017
卷号	699 页码:79-86
ISSN号	0925-8388
英文摘要	Transparent conductive ZnO films doped with 0-6 mol% of Al3+ (or AZO films) and AZO-rGO (rGO-reduced graphene oxide, similar to 0-0.5 g/L) nanocomposite films were deposited on silica glass substrates by sol-gel multilayer spin-coating, with annealing at 250 degrees C in vacuum. The effects of the processing conditions on the structure, optical and electrical properties of the AZO-rGO films, as well as the AZO thin films for comparison, were investigated by XRD, Raman spectroscopy, TEM and SEM, UV-Vis-NIR spectroscopy, and with the four-point prober and Hall effect measurements. Al3+ ions and rGO sheets existed in the composite films, and both of more Al3+ amount and more rGO could result in worse crystallinity of ZnO. More amount of rGO led to more rGO fiakers existed in the surface of the AZO-rGO films. Increasing Al-doping amount could not obviously affect the optical transmittances of the AZO-rGO films, but lead to the UV absorption edge of the films slightly blue-shifted. Optical transmittances of the AZO-rGO films decreased obviously with increasing the rGO ratio, but slightly decreased with increasing the annealing time. The minimum sheet resistance R-square could be obtained when Al-doping amount was similar to 2 mol% and rGO similar to 0.25 g/L: 50.1 k Omega/square for the AZO film and 15.2 k Omega/square El for the AZO-rGO film. Addition of rGO could improve the electric conductivity of AZO films. Longer time of vacuum-annealing could also improve the electric conductivity of the AZO-rGO films. For the AZO-rGO film doped with 2 mol% Al3+ and 10 mg rGO after vacuum-annealing for 12 h, Hall mobility was similar to 17.7 cm(2)/Vs and the carrier concentration was similar to 10.6 x 10(19)/cm(3). (C) 2016 Elsevier B.V. All rights reserved.
公开日期	2017-12-25
内容类型	期刊论文
源URL	[http://ir.nimte.ac.cn/handle/174433/13923]
专题	2017专题
推荐引用方式 GB/T 7714	Lu, Huanming,Yu, Xiayang,Xu, Jian,et al. Sol-gel derived Al-doped zinc oxide - Reduced graphene oxide nanocomposite thin films[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2017,699:79-86.
APA	Lu, Huanming,Yu, Xiayang,Xu, Jian,&Fang, Gang.(2017).Sol-gel derived Al-doped zinc oxide - Reduced graphene oxide nanocomposite thin films.JOURNAL OF ALLOYS AND COMPOUNDS,699,79-86.
MLA	Lu, Huanming,et al."Sol-gel derived Al-doped zinc oxide - Reduced graphene oxide nanocomposite thin films".JOURNAL OF ALLOYS AND COMPOUNDS 699(2017):79-86.