Microstructure and mechanical properties of Al-Mg-Ti-B coatings prepared by high power impulse magnetron sputtering (HIPIMS) at room temperature | |
Zhang, Congcong; Zhu, Ping; Huang, Feng; Ouyang, Jun; Tian, Yun | |
刊名 | SURFACE & COATINGS TECHNOLOGY
![]() |
2017 | |
卷号 | 322页码:25-30 |
ISSN号 | 0257-8972 |
英文摘要 | In this work, Al-Mg-Ti-B coatings were synthesized at room temperature via high power impulse magnetron sputtering (HIPIMS). The as-deposited Al-Mg-Ti-B coatings exhibited a dense and X-ray amorphous microstructure. It was demonstrated that the chemical composition and mechanical properties of Al-Mg-Ti-B coatings were significantly altered by applying different negative bias voltages during the HIPIMS process. The XPS results showed that oxygen concentration in the coatings was reduced from similar to 22 at.% to similar to 8 at% and the number of oxygen-boron bonds dropped with an increasing bias voltage, which contributed significantly to the improved mechanical properties. Nano-indentation results showed that the nano-hardness and elastic modulus of the HIPIMS Al-Mg-Ti-B coatings were as high as 37 GPa and 348 GPa, respectively. (C) 2017 Elsevier B.V. All rights reserved. |
公开日期 | 2017-12-25 |
内容类型 | 期刊论文 |
源URL | [http://ir.nimte.ac.cn/handle/174433/13682] ![]() |
专题 | 2017专题 |
推荐引用方式 GB/T 7714 | Zhang, Congcong,Zhu, Ping,Huang, Feng,et al. Microstructure and mechanical properties of Al-Mg-Ti-B coatings prepared by high power impulse magnetron sputtering (HIPIMS) at room temperature[J]. SURFACE & COATINGS TECHNOLOGY,2017,322:25-30. |
APA | Zhang, Congcong,Zhu, Ping,Huang, Feng,Ouyang, Jun,&Tian, Yun.(2017).Microstructure and mechanical properties of Al-Mg-Ti-B coatings prepared by high power impulse magnetron sputtering (HIPIMS) at room temperature.SURFACE & COATINGS TECHNOLOGY,322,25-30. |
MLA | Zhang, Congcong,et al."Microstructure and mechanical properties of Al-Mg-Ti-B coatings prepared by high power impulse magnetron sputtering (HIPIMS) at room temperature".SURFACE & COATINGS TECHNOLOGY 322(2017):25-30. |