Effect of irradiation damage on corrosion of 4H-SiC in FLiNaK molten salt | |
Li, JJ; Huang, HF; Huang, Q; Tang, M; Zhao, B; Ji, GW; Zhang, W; Xie, RB; Yan, L | |
刊名 | CORROSION SCIENCE |
2017 | |
卷号 | 125期号:-页码:194-197 |
关键词 | Silicon-carbide Fuel |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2017.05.028 |
文献子类 | 期刊论文 |
英文摘要 | The corrosion behavior of 4H-SiC in the FLiNaK molten salt (650 degrees C), pre-irradiated with 70-keV Si ions to 2.5 dpa at 650 degrees C, was investigated in order to clarify the effect of irradiation on corrosion. The irradiated region of 4H-SiC is peeled off by the molten salt, and the corrosion depth is nearly consistent with the irradiation damage depth. Molten salt corrosion leads to the loss of Si element and the formation of carbon-rich phase in irradiated 4H-SiC surface. The broken of Si-C bonds induced by irradiation plays a key role in the irradiation assisted corrosion of SiC. |
WOS关键词 | SILICON-CARBIDE ; FUEL |
语种 | 英语 |
WOS记录号 | WOS:000407535500019 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/28625] |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
推荐引用方式 GB/T 7714 | Li, JJ,Huang, HF,Huang, Q,et al. Effect of irradiation damage on corrosion of 4H-SiC in FLiNaK molten salt[J]. CORROSION SCIENCE,2017,125(-):194-197. |
APA | Li, JJ.,Huang, HF.,Huang, Q.,Tang, M.,Zhao, B.,...&Yan, L.(2017).Effect of irradiation damage on corrosion of 4H-SiC in FLiNaK molten salt.CORROSION SCIENCE,125(-),194-197. |
MLA | Li, JJ,et al."Effect of irradiation damage on corrosion of 4H-SiC in FLiNaK molten salt".CORROSION SCIENCE 125.-(2017):194-197. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论